| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 1.78 GPa | 258 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 47.0 MPa | 6820 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.47 GPa | 213 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.400 J/cm | 0.749 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.67 J/cm | 12.5 ft-lb/in | ASTM D4812 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+9 - 1.00e+11 ohm-cm | 1.00e+9 - 1.00e+11 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+9 - 1.00e+11 ohm | 1.00e+9 - 1.00e+11 ohm | ASTM D257 |
| Static Decay | <= 1.0 sec | <= 1.0 sec | 5000V to <50V; FTMS101B |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C @Thickness 3.20 mm | 151 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |