- 熔體流動速率 [g/10min]: 12.0
- 密度 [g/cm3]: 1.15
- 缺口沖擊強度: 0.481
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in3 | ASTM D-792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D-955 |
| Melt Flow | 12 g/10 min @Load 3.80 kg, Temperature 230 °C | 12 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 49.6 MPa | 7200 psi | ASTM D-638 |
| Elongation at Break | 5.3 % | 5.3 % | ASTM D-638 |
| Modulus of Elasticity | 2.38 GPa | 345 ksi | ASTM D-638 |
| Flexural Strength | 48.3 MPa | 7000 psi | ASTM D-790 |
| Izod Impact, Notched | 0.481 J/cm @Thickness 6.35 mm | 0.900 ft-lb/in @Thickness 0.250 in | ASTM D-256 |
| Gardner Impact | 3.16 J @Thickness 3.17 mm | 2.33 ft-lb @Thickness 0.125 in | Falling Weight; ASTM D-3029 GB |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 100 μm/m-°C | 55.6 μin/in-°F | ASTM D-696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.3 °C | 164 °F | ASTM D-648 |
| Vicat Softening Point | 108 °C | 226 °F | ASTM D-1525 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 2.0 % | <= 2.0 % | ASTM D-1003 |
| Transmission, Visible | 90 % | 90 % | ASTM D-1003 |