- 熔體流動速率 [g/10min]: 1.6
- 密度 [g/cm3]: 1.19
- 缺口沖擊強度: 0.16
- 彎曲強度 [MPa]: 72.4
- 透光率 [%]: 92.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in3 | ASTM D792 |
| Melt Flow | 1.6 g/10 min | 1.6 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 72.4 MPa | 10500 psi | ASTM D638 |
| Elongation at Break | 6 % | 6 % | ASTM D638 |
| Modulus of Elasticity | 3.65 GPa | 529 ksi | ASTM D638 |
| Flexural Strength | 117.2 MPa | 17000 psi | ASTM D790 |
| Izod Impact, Notched | 0.160 J/cm | 0.300 ft-lb/in | ASTM D256 |
| Gardner Impact | 0.226 J | 0.167 ft-lb | Falling Weight; ASTM D3029GB |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | UL746 ABC Relative Thermal Index |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 92 % | 92 % | ASTM D1003 |