- 熔體流動(dòng)速率 [g/10min]: 2.7
- 密度 [g/cm3]: 1.19
- 缺口沖擊強(qiáng)度: 0.16
- 彎曲強(qiáng)度 [MPa]: 68.0
- 透光率 [%]: 92.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in3 | ASTM D792 |
| Melt Flow | 2.7 g/10 min | 2.7 g/10 min | Condition 230/2-8; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 68.0 MPa | 9860 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Modulus of Elasticity | 3.00 GPa | 435 ksi | ASTM D638 |
| Flexural Strength | 118 MPa | 17100 psi | ASTM D790 |
| Izod Impact, Notched | 0.160 J/cm | 0.300 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | UL 746 ABC |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ASTM D648 |
| Vicat Softening Point | 102 °C | 216 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 92 % | 92 % | Luminous Transmittance, ASTM D1003 |