- 熔體流動(dòng)速率 [g/10min]: 14.0
- 密度 [g/cm3]: 1.19
- 缺口沖擊強(qiáng)度: 0.16
- 透光率 [%]: 92.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in3 | ASTM D-792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D-955 |
| Melt Flow | 14 g/10 min @Load 3.80 kg, Temperature 230 °C | 14 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 55.8 MPa | 8100 psi | ASTM D-638 |
| Elongation at Break | 2.6 % | 2.6 % | ASTM D-638 |
| Modulus of Elasticity | 2.89 GPa | 419 ksi | ASTM D-638 |
| Flexural Strength | 102 MPa | 14800 psi | ASTM D-790 |
| Izod Impact, Notched | 0.160 J/cm @Thickness 6.35 mm | 0.300 ft-lb/in @Thickness 0.250 in | ASTM D-256 |
| Gardner Impact | 0.226 J @Thickness 3.17 mm | 0.167 ft-lb @Thickness 0.125 in | Falling Weight; ASTM D-3029 GB |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 60.0 μm/m-°C | 33.3 μin/in-°F | ASTM D-696 |
| Maximum Service Temperature, Air | 85.0 °C | 185 °F | UL-746 ABC |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C | 168 °F | ASTM D-648 |
| Vicat Softening Point | 93.9 °C | 201 °F | ASTM D-1525 |
| Flammability, UL94 | HB | HB | |
| Optical Properties | Metric | English | Comments |
| Haze | <= 1.0 % | <= 1.0 % | ASTM D-1003 |
| Transmission, Visible | 92 % | 92 % | ASTM D-1003 |