- 熔體流動速率 [g/10min]: 2.2
- 密度 [g/cm3]: 1.19
- 彎曲強度 [MPa]: 69.0
- 透光率 [%]: 92.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in3 | ASTM D792 |
| Melt Flow | 2.2 g/10 min | 2.2 g/10 min | Condition 230/2-8; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 69.0 MPa | 10000 psi | ASTM D638 |
| Elongation at Break | 4.6 % | 4.6 % | ASTM D638 |
| Modulus of Elasticity | 3.40 GPa | 493 ksi | ASTM D638 |
| Flexural Strength | 105 MPa | 15200 psi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | UL 746 ABC |
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | ASTM D648 |
| Vicat Softening Point | 104 °C | 219 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 92 % | 92 % | Luminous Transmittance, ASTM D1003 |