- 熔體流動速率 [g/10min]: 35.0
- 缺口沖擊強度: 0.16
- 拉伸強度 [MPa]: 60.7
- 斷裂伸長率 [%]: 103
- 彎曲模量 [MPa]: 2.90
- 透光率 [%]: 93.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 35 g/10 min @Load 3.80 kg, Temperature 230 °C | 35 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 60.7 MPa | 8800 psi | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Yield Strength | 103 MPa | 14900 psi | ASTM D790 |
| Flexural Modulus | 2.90 GPa | 420 ksi | ASTM D790 |
| Izod Impact, Notched | 0.160 J/cm @Thickness 3.17 mm, Temperature 22.8 °C | 0.300 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.9 °C @Thickness 3.17 mm | 183 °F @Thickness 0.125 in | annealed; ASTM D648 |
| Vicat Softening Point | 95.0 °C | 203 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ASTM D542 |
| Haze | 0.50 % | 0.50 % | ASTM D1003 |
| Transmission, Visible | 93 % | 93 % | Total light Transmission; ASTM D1003 |