- 熔體流動(dòng)速率 [g/10min]: 20.0
- 缺口沖擊強(qiáng)度: 0.834
- 拉伸強(qiáng)度 [MPa]: 66.7
- 斷裂伸長(zhǎng)率 [%]: 103
- 彎曲模量 [MPa]: 2.79
- 熱變形溫度 [℃]: 94.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.040 | 0.040 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm | 0.0030 - 0.0050 in/in @Thickness 0.126 in | ASTM D955 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 250 °C | 20 g/10 min @Load 4.76 lb, Temperature 482 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 66.7 MPa @Thickness 3.20 mm | 9670 psi @Thickness 0.126 in | 50mm/min; ASTM D638 |
| Flexural Yield Strength | 103 MPa @Thickness 3.20 mm | 14900 psi @Thickness 0.126 in | 10mm/min; ASTM D790 |
| Flexural Modulus | 2.79 GPa @Thickness 3.20 mm | 405 ksi @Thickness 0.126 in | 10mm/min; ASTM D790 |
| Izod Impact, Notched | 0.834 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 1.56 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C @Thickness 6.40 mm | 201 °F @Thickness 0.252 in | Unannealed; ASTM D648 |
| UL RTI, Electrical | 80.0 °C | 176 °F | |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | |
| Flammability, UL94 | V-0 @Thickness >=1.20 mm | V-0 @Thickness >=0.0472 in | |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 230 - 270 °C | 446 - 518 °F | Injection Molding |
| Middle Barrel Temperature | 235 - 270 °C | 455 - 518 °F | Injection Molding |
| Front Barrel Temperature | 235 - 270 °C | 455 - 518 °F | Injection Molding |
| Nozzle Temperature | 235 - 270 °C | 455 - 518 °F | Injection Molding |
| Melt Temperature | 245 - 270 °C | 473 - 518 °F | Injection Molding |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | Injection Molding |
| Drying Temperature | 75.0 - 85.0 °C | 167 - 185 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 0.981 - 1.96 MPa | 142 - 284 psi | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |