- 缺口沖擊強度: 0.451
- 拉伸強度 [MPa]: 54.9
- 斷裂伸長率 [%]: 85.3
- 彎曲模量 [MPa]: 2.16
- 熱變形溫度 [℃]: 100.0
- 透光率 [%]: 75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0070 in/in @Thickness 0.126 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 54.9 MPa @Thickness 3.20 mm | 7970 psi @Thickness 0.126 in | 50mm/min; ASTM D638 |
| Elongation at Break | 30 % @Thickness 3.20 mm | 30 % @Thickness 0.126 in | 50mm/min; ASTM D638 |
| Flexural Yield Strength | 85.3 MPa @Thickness 3.20 mm | 12400 psi @Thickness 0.126 in | 15mm/min; ASTM D790 |
| Flexural Modulus | 2.16 GPa @Thickness 3.20 mm | 313 ksi @Thickness 0.126 in | 15mm/min; ASTM D790 |
| Izod Impact, Notched | >= 0.451 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | >= 0.845 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 2.00e+12 ohm | 2.00e+12 ohm | IEC 60093 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C @Thickness 6.40 mm | 212 °F @Thickness 0.252 in | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C @Thickness 6.40 mm | 194 °F @Thickness 0.252 in | ASTM D648 |
| Optical Properties | Metric | English | Comments |
| Haze | 10 % | 10 % | ASTM D1003 |
| Transmission, Visible | 75 % | 75 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Middle Barrel Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Front Barrel Temperature | 200 - 220 °C | 392 - 428 °F | Injection Molding |
| Nozzle Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection Molding |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Injection Molding |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Injection Molding |
| Back Pressure | 0.490 - 0.981 MPa | 71.1 - 142 psi | Injection Molding |
| Screw Speed | <= 80 rpm | <= 80 rpm | Injection Molding |