- 密度 [g/cm3]: 1.44
- 缺口沖擊強(qiáng)度: 0.64
- 斷裂伸長(zhǎng)率 [%]: 76.0
- 彎曲強(qiáng)度 [MPa]: 52.0
- 彎曲模量 [MPa]: 2.989
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in3 | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
| Elongation at Break | 195 % | 195 % | ASTM D638 |
| Flexural Yield Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 2.989 GPa | 433.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.640 J/cm @Temperature 23.0 °C | 1.20 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 74.4 °C | 166 °F | annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 - 182 °C | 320 - 360 °F | Barrel Temp |
| Middle Barrel Temperature | 160 - 182 °C | 320 - 360 °F | |
| Adapter Temperature | 171 - 177 °C | 340 - 350 °F | |
| Die Temperature | 171 - 177 °C | 340 - 350 °F | |
| Dry Time | 0.0 hour | 0.0 hour | Drying typically not required |