- 熔體流動速率 [g/10min]: 1.5
- 密度 [g/cm3]: 1.19
- 吸水率 [%]: 1.9
- 拉伸強度 [MPa]: 86.0
- 熱變形溫度 [℃]: 96.0
- 透光率 [%]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in3 | |
| Water Absorption | 1.9 % | 1.9 % | |
| Moisture Absorption at Equilibrium | 0.30 % | 0.30 % | Humidity Absorption |
| Melt Flow | 1.5 g/10 min @Load 3.80 kg, Temperature 230 °C | 1.5 g/10 min @Load 8.38 lb, Temperature 446 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 86.0 MPa | 12500 psi | 50 mm/min |
| Elongation at Break | 6.0 % | 6.0 % | Nominal Strain; 50 mm/min |
| Tensile Modulus | 3.30 GPa | 479 ksi | 1 mm/min |
| Charpy Impact Unnotched | 2.00 J/cm2 | 9.52 ft-lb/in2 | |
| Charpy Impact, Notched | 0.200 J/cm2 | 0.952 ft-lb/in2 | |
| Tensile Creep Modulus, 1 hour | 2700 MPa | 392000 psi | |
| Tensile Creep Modulus, 1000 hours | 1800 MPa | 261000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz | 3.2 @Frequency 1e+6 Hz | |
| 3.7 @Frequency 100 Hz | 3.7 @Frequency 100 Hz | ||
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | |
| Dissipation Factor | 0.040 @Frequency 1e+6 Hz | 0.040 @Frequency 1e+6 Hz | |
| 0.050 @Frequency 100 Hz | 0.050 @Frequency 100 Hz | ||
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 65.0 μm/m-°C @Temperature 20.0 °C | 36.1 μin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C | 205 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | |
| Vicat Softening Point | 96.0 °C | 205 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 80 % | 80 % | Mfr. reports 'Transparent' but doesn't quantify. |