- 熔體流動速率 [g/10min]: 1.6
- 密度 [g/cm3]: 1.15
- 缺口沖擊強度: 0.64
- 彎曲強度 [MPa]: 40.0
- 透光率 [%]: 90.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in3 | ASTM D792 |
| Melt Flow | 1.6 g/10 min | 1.6 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Modulus of Elasticity | 1.38 GPa | 200 ksi | ASTM D638 |
| Flexural Strength | 46.9 MPa | 6800 psi | ASTM D790 |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Impact Test | 6.10 J | 4.50 ft-lb | Falling weight impact per ASTM D3029 GB |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | ASTM D648 |
| Vicat Softening Point | 100 °C | 212 °F | Rate A, ASTM D1525 |
| Flammability, UL94 | HB | HB | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.8 % | 90.8 % | ASTM D1003 |