- 熔體流動速率 [g/10min]: 2.8
- 密度 [g/cm3]: 1.16
- 缺口沖擊強度: 0.59
- 彎曲強度 [MPa]: 42.1
- 透光率 [%]: 90.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in3 | ASTM D792 |
| Melt Flow | 2.8 g/10 min | 2.8 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 42.1 MPa | 6110 psi | ASTM D638 |
| Elongation at Break | 14 % | 14 % | ASTM D638 |
| Modulus of Elasticity | 2.03 GPa | 294 ksi | ASTM D638 |
| Flexural Strength | 61.4 MPa | 8910 psi | ASTM D790 |
| Izod Impact, Notched | 0.590 J/cm | 1.11 ft-lb/in | ASTM D256 |
| Impact Test | 5.50 J | 4.06 ft-lb | Falling weight impact per ASTM D3029 GB |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | ASTM D648 |
| Vicat Softening Point | 108 °C | 226 °F | Rate A, ASTM D1525 |
| Flammability, UL94 | HB | HB | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.8 % | 90.8 % | ASTM D1003 |