- 熔體流動速率 [g/10min]: 4.1
- 吸水率 [%]: 0.4
- 缺口沖擊強度: 0.481
- 彎曲強度 [MPa]: 36.5
- 彎曲模量 [MPa]: 1.86
- 熱變形溫度 [℃]: 87.8
- 透光率 [%]: 91.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | weight gain after 24 hr. immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0080 cm/cm | 0.0030 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 4.1 g/10 min @Load 3.80 kg, Temperature 230 °C | 4.1 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 38 | 38 | ASTM D785 |
| Tensile Strength, Ultimate | 36.5 MPa | 5300 psi | ASTM D638 |
| Tensile Modulus | 1.86 GPa | 270 ksi | ASTM D638 |
| Flexural Strength | <= 71.0 MPa | <= 10300 psi | ASTM D790 |
| Flexural Modulus | 1.86 GPa | 270 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm | 0.900 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.216 W/m-K | 1.50 BTU-in/hr-ft2-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.8 °C | 181 °F | annealed; ASTM D648 |
| Vicat Softening Point | 80.0 °C | 176 °F | 50°C/hr; 50N; ASTM D1525 |
| 92.8 °C | 199 °F | 50°C/hr; 10N; ASTM D1525 | |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 @Temperature 22.8 °C | 1.49 @Temperature 73.0 °F | ND; ASTM D542 |
| Haze | <= 2.0 % @Thickness 3.17 mm | <= 2.0 % @Thickness 0.125 in | ASTM D1003 |
| Transmission, Visible | 91 % @Thickness 3.17 mm | 91 % @Thickness 0.125 in | ASTM D1003 |