- 熔體流動速率 [g/10min]: 3.2
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 0.32
- 彎曲強度 [MPa]: 48.3
- 彎曲模量 [MPa]: 2.62
- 熱變形溫度 [℃]: 91.1
- 透光率 [%]: 91.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | weight gain after 24 hr. immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 3.2 g/10 min @Load 3.80 kg, Temperature 230 °C | 3.2 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 68 | 68 | ASTM D785 |
| Tensile Strength, Ultimate | 48.3 MPa | 7000 psi | ASTM D638 |
| Tensile Modulus | 2.62 GPa | 380 ksi | ASTM D638 |
| Flexural Strength | <= 99.3 MPa | <= 14400 psi | ASTM D790 |
| Flexural Modulus | 2.62 GPa | 380 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.600 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.202 W/m-K | 1.40 BTU-in/hr-ft2-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 91.1 °C | 196 °F | annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | annealed; ASTM D648 |
| Vicat Softening Point | 90.0 °C | 194 °F | 50°C/hr; 50N; ASTM D1525 |
| 98.9 °C | 210 °F | 50°C/hr; 10N; ASTM D1525 | |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 @Temperature 22.8 °C | 1.49 @Temperature 73.0 °F | ND; ASTM D542 |
| Haze | <= 2.0 % @Thickness 3.17 mm | <= 2.0 % @Thickness 0.125 in | ASTM D1003 |
| Transmission, Visible | 91 % @Thickness 3.17 mm | 91 % @Thickness 0.125 in | ASTM D1003 |