- 熔體流動速率 [g/10min]: 4.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.935 g/cc | 0.935 g/cc | ISO 1183 |
| Vinyl Acetate Content | 14 % | 14 % | |
| Thickness | 40.0 microns | 1.57 mil | for samples tested on this data sheet |
| 15.0 - 100 microns | 0.591 - 3.94 mil | possible range, depending on extrusion conditions | |
| Melt Flow | 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 6.50 MPa | 943 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 4.90 MPa | 711 psi | ISO 527-3 |
| Film Elongation at Break, MD | 370 % | 370 % | ISO 527-3 |
| Film Elongation at Break, TD | 650 % | 650 % | ISO 527-3 |
| Modulus of Elasticity | 0.0620 GPa | 8.99 ksi | ISO 527-2 |
| Elmendorf Tear Strength, MD | 3.70 g/micron | 94.0 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 4.50 g/micron | 114 g/mil | ISO 6383-2 |
| Dart drop Test | 300 g | 0.662 lb | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 27.0 MPa | 3920 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 90.0 °C | 194 °F | ISO 11357 |
| Vicat Softening Point | 68.0 °C | 154 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.0 % | 2.0 % | ISO 14782 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 140 - 170 °C | 284 - 338 °F | |