- 熔體流動速率 [g/10min]: 2.5
- 拉伸強度 [MPa]: 7.0
- 彎曲模量 [MPa]: 0.100
- 脆化溫度 [℃]: -80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.925 g/cc | 0.925 g/cc | ISO 1183 |
| Vinyl Acetate Content | 7.0 % | 7.0 % | Internal Method |
| Melt Flow | 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 95 | 95 | ISO 868/A |
| Hardness, Shore D | 43 | 43 | ISO 868/A |
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ISO 527 |
| Flexural Modulus | 0.100 GPa | 14.5 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 101 °C | 214 °F | Internal Method |
| Vicat Softening Point | 78.0 °C @Load 1.00 kg | 172 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -80.0 °C | <= -112 °F | ASTM D746 |