- 熔體流動速率 [g/10min]: 2.0
- 脆化溫度 [℃]: -80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.923 g/cc | 0.923 g/cc | ISO 1183 |
| Vinyl Acetate Content | 4.5 % | 4.5 % | Internal Method |
| Thickness | 30.0 - 150 microns | 1.18 - 5.91 mil | Recommended |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 96 | 96 | ISO 868/A |
| Hardness, Shore D | 44 | 44 | ISO 868/A |
| Film Tensile Strength at Yield, MD | 7.00 MPa | 1020 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 7.00 MPa | 1020 psi | ISO 527-3 |
| Film Elongation at Break, MD | 300 % | 300 % | ISO 527-3 |
| Film Elongation at Break, TD | 560 % | 560 % | ISO 527-3 |
| Coefficient of Friction, Dynamic | >= 0.20 | >= 0.20 | ISO 8295 |
| Elmendorf Tear Strength, MD | 2.5475 g/micron | 64.706 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 3.8722 g/micron | 98.354 g/mil | ISO 6383-2 |
| Dart drop Test | 400 g | 0.882 lb | F50; ISO 7765-1 |
| Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ISO 527-3 |
| 1% Secant Modulus, MD | 140 MPa | 20300 psi | ISO 527-3 |
| 1% Secant Modulus, TD | 150 MPa | 21800 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 103 °C | 217 °F | Internal Method |
| Vicat Softening Point | 82.0 °C @Load 1.00 kg | 180 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -80.0 °C | <= -112 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
| Haze | 6.0 % | 6.0 % | ISO 14782 |
| Gloss | 65 % | 65 % | 45°; ASTM D2457 |