- 熔體流動(dòng)速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.923
- 拉伸強(qiáng)度 [MPa]: 2.7
- 彎曲強(qiáng)度 [MPa]: 1.5
- 彎曲模量 [MPa]: 0.00440
- 透光率 [%]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.923 - 0.980 g/cc | 0.0333 - 0.0354 lb/in3 | Average value: 0.945 g/cc Grade Count:67 |
| Apparent Bulk Density | 0.449 - 0.577 g/cc | 0.0162 - 0.0208 lb/in3 | Average value: 0.534 g/cc Grade Count:9 |
| Viscosity | 140 - 40000 cP @Temperature 121 - 190 °C | 140 - 40000 cP @Temperature 250 - 374 °F | Average value: 495000 cP Grade Count:42 |
| 300000 - 1.90e+6 cP @Temperature 190 - 190 °C | 300000 - 1.90e+6 cP @Temperature 374 - 374 °F | Average value: 495000 cP Grade Count:22 | |
| 300000 - 1.90e+6 cP @Shear Rate 50.0 - 50.0 1/s | 300000 - 1.90e+6 cP @Shear Rate 50.0 - 50.0 1/s | Average value: 495000 cP Grade Count:22 | |
| Viscosity Measurement | 0.700 - 0.700 @Temperature 30.0 - 30.0 °C | 0.700 - 0.700 @Temperature 86.0 - 86.0 °F | Average value: 0.700 Grade Count:1 |
| Environmental Stress Crack Resistance | >= 300 hour @Temperature 50.0 - 50.0 °C | >= 300 hour @Temperature 122 - 122 °F | Average value: 300 hour Grade Count:3 |
| >= 300 hour @Thickness 2.00 - 2.00 mm | >= 300 hour @Thickness 0.0787 - 0.0787 in | Average value: 300 hour Grade Count:3 | |
| Vinyl Acetate Content | 17.0 - 44.0 % | 17.0 - 44.0 % | Average value: 27.6 % Grade Count:31 |
| Melt Flow | 0.800 - 900 g/10 min | 0.800 - 900 g/10 min | Average value: 113 g/10 min Grade Count:64 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 40.0 - 85.0 | 40.0 - 85.0 | Average value: 69.8 Grade Count:34 |
| Hardness, Shore D | 15.0 - 31.0 | 15.0 - 31.0 | Average value: 22.9 Grade Count:11 |
| Tensile Strength, Ultimate | 1.50 - 27.0 MPa | 218 - 3920 psi | Average value: 7.37 MPa Grade Count:36 |
| Tensile Strength, Yield | 2.70 - 6.50 MPa | 392 - 943 psi | Average value: 4.82 MPa Grade Count:4 |
| Elongation at Break | 50.0 - 1300 % | 50.0 - 1300 % | Average value: 668 % Grade Count:38 |
| Modulus of Elasticity | 0.00300 - 0.100 GPa | 0.435 - 14.5 ksi | Average value: 0.0677 GPa Grade Count:3 |
| Flexural Modulus | 0.00440 - 0.0414 GPa | 0.638 - 6.00 ksi | Average value: 0.0221 GPa Grade Count:12 |
| Dart Drop, Total Energy | 24.4048 - 24.4048 J @Temperature -40.0 - -40.0 °C | 18.0000 - 18.0000 ft-lb @Temperature -40.0 - -40.0 °F | Average value: 24.4 J Grade Count:1 |
| Seal Strength | 1200 - 4500 g/25 mm | 1200 - 4500 g/in | Average value: 2860 g/25 mm Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 48.0 - 102 °C | 118 - 216 °F | Average value: 74.7 °C Grade Count:66 |
| Maximum Service Temperature, Air | 51.7 - 78.9 °C | 125 - 174 °F | Average value: 68.2 °C Grade Count:29 |
| Vicat Softening Point | 40.0 - 181 °C | 104 - 358 °F | Average value: 63.5 °C Grade Count:58 |
| Minimum Service Temperature, Air | -45.6 - -17.8 °C | -50.0 - 0.000 °F | Average value: -28.9 °C Grade Count:29 |
| Ring & Ball Softening Point | 76.0 - 183 °C | 169 - 361 °F | Average value: 111 °C Grade Count:17 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.31 - 1.49 | 1.31 - 1.49 | Average value: 1.43 Grade Count:3 |
| Transmission, Visible | 80.0 - 90.0 % | 80.0 - 90.0 % | Average value: 83.3 % Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 200 - 275 °C | 392 - 527 °F | Average value: 233 °C Grade Count:38 |
| Nozzle Temperature | 185 - 275 °C | 365 - 527 °F | Average value: 234 °C Grade Count:22 |
| Pot Life | 0.0833 - 1.00 min | 0.0833 - 1.00 min | Average value: 0.449 min Grade Count:29 |