加工/物理特性	值(Value)	單位(Unit)	測試標準(Test Standard)
ASTM數(shù)據(jù)(ASTM Data)
熔體流動指數(shù)(Melt Flow Index)	17.5	g/10min	ASTM D 1238
溫度(Temperature)	300	°C	-
負載(Load)	1.2	kg	-
模具收縮(Mold Shrinkage) (MD)	0.006	mm/mm	ASTM D 955
密度(Density) (73°F)	1200	kg/m3	ASTM D 792
吸水率(Water Absorption) (24hr)	0.15	%	ASTM D 570
吸水率(Water Absorption) (Equilibrium)	0.35	%	ASTM D 570

流變性能(Rheological properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數(shù)據(jù)
熔體體積流動速率(Melt volume-flow rate) (MVR)	16	cm3/10min	ISO 1133
溫度(Temperature)	300	°C	ISO 1133
負載(Load)	1.2	kg	ISO 1133

機械性能(機械性能(Mechanical properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數(shù)據(jù)
拉伸模量(Tensile Modulus)	2350	MPa	ISO 527-1/-2
屈服應力(Yield stress)	63	MPa	ISO 527-1/-2
屈服應變(Yield strain)	6	%	ISO 527-1/-2
破壞時應變(Stress at break)	65	MPa	ISO 527-1/-2
破壞時應變(Strain at break)	>50	%	ISO 527-1/-2
簡支梁沖擊強度(Charpy impact strength) (+23°C)	N	kJ/m2	ISO 179/1eU
彎曲彈性模量(Flexural modulus) (23°C)	2300	MPa	ISO 178
懸臂梁式?jīng)_擊切口 (23°C)	12	kJ/m2	ISO 180/1A
懸臂梁式?jīng)_擊切口	10	kJ/m2	ISO 180/1A
溫度(Temperature)	-30	°C	ISO 180/1A
ASTM數(shù)據(jù)(ASTM Data)
拉伸模量(Tensile Modulus)	2370	MPa	ASTM D 638
抗拉強度(Tensile Strength) at Yield	62	MPa	ASTM D 638
抗拉強度(Tensile Strength) at Break	68	MPa	ASTM D 638
屈服伸長率(Elongation at Yield)	7	%	ASTM D 638
斷裂伸長率(Elongation at Break)	125	%	ASTM D 638
彎曲彈性模量(彎曲彈性模量(Flexural Modulus))	2340	MPa	ASTM D 790
洛氏硬度(Rockwell Hardness)	R 118	-	ASTM D 785
Taber Abrasion Resistance	10	mg/1000 cycles	ASTM D 1044
懸臂梁式?jīng)_擊切口 (1/8 in)	0.667	kJ/m	ASTM D 256
懸臂梁式?jīng)_擊切口 (Low-溫度(Temperature))	N	kJ/m	ASTM D 256
溫度(Temperature)	-30	°C	ASTM D 256

熱性能(熱性能(Thermal properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數(shù)據(jù)
維卡軟化溫度（50℃/ h的50N）Vicat softening temperature	140	°C	ISO 306
COEFF線性熱(Coeff. of linear therm. expansion) (parallel)	70	E-6/K	ISO 11359-1/-2
COEFF線性熱(Coeff. of linear therm. expansion) (normal)	70	E-6/K	ISO 11359-1/-2
ASTM數(shù)據(jù)(ASTM Data)
UL 94 阻燃等級(Flame rating)	HB	-	UL 94
厚度測試(Thickness tested)	1.47	mm	-
熱膨脹系數(shù)(Coefficient of Thermal Expansion) (MD)	68	E-6/K	ASTM D 696
熱膨脹系數(shù)(Coefficient of Thermal Expansion) (TD)	68.4	E-6/K	ASTM D 696
Vicat 溫度(Temperature)	154	°C	ASTM D 1525
Thermal Conductivity (melt state)	0.19	W/(m K)	ASTM C 177
Specific Heat	1.25	J/(kg K)	ASTM C 351

電氣性能(Electrical properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ASTM數(shù)據(jù)(ASTM Data)
絕緣強度(Dielectric Strength) (Short Time)	14.9	kV/mm	ASTM D 149
耗散因數(shù)(Dissipation Factor) (60 Hz)	0.0009	-	ASTM D 150
耗散因數(shù)(Dissipation Factor) (1 MHz)	0.01	-	ASTM D 150
介電常數(shù)(Dielectric Constant) (60 Hz)	3.17	-	ASTM D 150
介電常數(shù)(Dielectric Constant) (1 MHz)	2.96	-	ASTM D 150
體積電阻率(Volume Resistivity)	>1E15	Ohm*cm	ASTM D 257

其他屬性(Other properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數(shù)據(jù)
吸水率(Water absorption)	0.35	%	Sim. to ISO 62
吸濕性(Humidity absorption)	0.15	%	Sim. to ISO 62
密度(Density)	1200	kg/m3	ISO 1183

Optical properties	值(Value)	單位(Unit)	測試標準(Test Standard)
ASTM數(shù)據(jù)(ASTM Data)
Haze	1	%	ASTM D 1003
Light Transmittance	88	%	ASTM D 1003
Index of Refraction	1.59	-	ASTM D 542

CharacteristicsProcessingInjection MoldingAdditivesRelease agentEcological valuationUS Pharmacopeia Class VI ApprovedApplicationsMedicalRegional Availability .

Lexan HP2JP|PC|沙特基礎