Ultramid? HPN 9362|PA6-MD40|BASF

Product TextsUltramid? HPN 9362 is a 40% mineral reinforced, impact modified Polyamid 6 injection molding compound. It is one of the High Productivity Polyamid series having improved surface appearance while reducing cycle time.

機械性能(機械性能(Mechanical properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	4330 / 2900	MPa	ISO 527-1/-2
屈服應力(Yield stress)	65 / 45	MPa	ISO 527-1/-2
屈服應變(Yield strain)	3 / 27	%	ISO 527-1/-2
斷裂拉伸應變(Nominal strain at break)	15 / 30	%	ISO 527-1/-2
簡支梁缺口沖擊強度(Charpy notched impact strength) (+23°C)	6 / -	kJ/m2	ISO 179/1eA

熱性能(熱性能(Thermal properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
熔化溫度(熔化溫度(Melting temperature)) (10°C/min)	220 / *	°C	ISO 11357-1/-3
燃燒性(球壓痕硬度(Burning behav)). at thickness h	HB / *	class	IEC 60695-11-10
厚度測試(Thickness tested)	0.8 / *	mm	IEC 60695-11-10
UL 識別(recognition)	UL / *	-	-

電氣性能(Electrical properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
體積電阻率(Volume resistivity)	>1E13 / -	Ohm*m	IEC 60093

其他屬性(Other properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
吸水率(Water absorption)	4.9 / *	%	Sim. to ISO 62
吸濕性(Humidity absorption)	1.4 / *	%	Sim. to ISO 62
密度(Density)	1410 / *	kg/m3	ISO 1183

Test specimen production	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
Injection Molding, melt temperature	275	°C	ISO 294
Injection Molding, mold temperature	95	°C	ISO 10724

Diagrams Water content: 0.12% If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level. Alternatively, please contact your BASF representative. Packing pressure affects the final part and can be use It should be applied and maintained until the gate area is completely frozen off.A maximum of 3.5 bar (50 psi) is recommended to minimize glass fiber breakage. Surface appearance is directly affected by injection rateDisclaimerCopyright M-Base .

關鍵詞:
BASF
PA6-MD40
Ultramid? HPN 9362