Ultramid? TG7S BK-102|PA6-GF35|BASF

Product TextsUltramid? TG7S is a 34% glass reinforced, heat stabilized, impact modified Polyamid 6 injection molding grade. It was developed to meet the demanding requirements of the first North American seat cushion pan/frame to bemade of an engineering plastic as opposed to metal. This material passed the Key end-use submarine impact test for General Motors H-Car Seat Pan Frame. TG7S exhibits improved strength, stiffness and notched impact properties over Ultramid? 8333G HI, at a significantly lower costThis material is also available in black.

流變性能(Rheological properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
熔體體積流動速率(Melt volume-flow rate) (MVR)	6 / *	cm3/10min	ISO 1133
溫度(Temperature)	235 / *	°C	ISO 1133
負載(Load)	5 / *	kg	ISO 1133

機械性能(機械性能(Mechanical properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	9500 / -	MPa	ISO 527-1/-2
破壞時應變(Stress at break)	165 / -	MPa	ISO 527-1/-2
破壞時應變(Strain at break)	2.5 / -	%	ISO 527-1/-2
簡支梁缺口沖擊強度(Charpy notched impact strength) (+23°C)	22 / -	kJ/m2	ISO 179/1eA

熱性能(熱性能(Thermal properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
熔化溫度(熔化溫度(Melting temperature)) (10°C/min)	220 / *	°C	ISO 11357-1/-3
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	208 / *	°C	ISO 75-1/-2
溫度負荷變形(Temp. of deflection under load) (0.45 MPa)	220 / *	°C	ISO 75-1/-2

其他屬性(Other properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
密度(Density)	1370 / -	kg/m3	ISO 1183

Diagrams Water content: 0.08% If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level. Alternatively, please contact your BASF representative. Packing pressure affects the final part and can be used effectively in controlling sink It should be applied and maintained until the gate area is completely frozen off.A maximum of 3.5 bar (50 psi) is recommended to minimize glass fiber breakage. Surface appearance is directly affected by injection rate.DisclaimerCopyright M-Base .