Product TextsChemical abbreviation according to ISO 1043-1: POM 20 % glass fibers; high5 mm as UL 94 HB, temperature index UL 746 B, electrical 105 °C,5	cm3/10min	ISO 1133
溫度(Temperature)	190	°C	ISO 1133
負載(Load)	2.16	kg	ISO 1133

機械性能(機械性能(Mechanical properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	7200	MPa	ISO 527-1/-2
破壞時應變(Stress at break)	120	MPa	ISO 527-1/-2
破壞時應變(Strain at break)	3	%	ISO 527-1/-2
Tensile creep modulus (1h)	6500	MPa	ISO 899-1
Tensile creep modulus (1000h)	4000	MPa	ISO 899-1
簡支梁沖擊強度(Charpy impact strength) (+23°C)	35	kJ/m2	ISO 179/1eU
簡支梁沖擊強度(Charpy impact strength) (-30°C)	40	kJ/m2	ISO 179/1eU
簡支梁缺口沖擊強度(Charpy notched impact strength) (+23°C)	8	kJ/m2	ISO 179/1eA
簡支梁缺口沖擊強度(Charpy notched impact strength) (-30°C)	8	kJ/m2	ISO 179/1eA

熱性能(熱性能(Thermal properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
熔化溫度(熔化溫度(Melting temperature)) (10°C/min)	166	°C	ISO 11357-1/-3
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	159	°C	ISO 75-1/-2
溫度負荷變形(Temp. of deflection under load) (8.00 MPa)	105	°C	ISO 75-1/-2
維卡軟化溫度（50℃/ h的50N）Vicat softening temperature	157	°C	ISO 306
COEFF線性熱(Coeff. of linear therm. expansion) (parallel)	50	E-6/K	ISO 11359-1/-2
COEFF線性熱(Coeff. of linear therm. expansion) (normal)	80	E-6/K	ISO 11359-1/-2
燃燒性(球壓痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB	class	IEC 60695-11-10
厚度測試(Thickness tested)	1.5	mm	IEC 60695-11-10
UL 識別(recognition)	UL	-	-
燃燒性(球壓痕硬度(Burning behav)). at thickness h	HB	class	IEC 60695-11-10
厚度測試(Thickness tested)	3.0	mm	IEC 60695-11-10
UL 識別(recognition)	UL	-	-

電氣性能(Electrical properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
相對介電常數(Relative permittivity) (100Hz)	4.3	-	IEC 60250
相對介電常數(Relative permittivity) (1MHz)	4.3	-	IEC 60250
耗散因數(耗散因數(Dissipation factor)) (100Hz)	30	E-4	IEC 60250
耗散因數(耗散因數(Dissipation factor)) (1MHz)	60	E-4	IEC 60250
體積電阻率(Volume resistivity)	1E12	Ohm*m	IEC 60093
表面電阻率(Surface resistivity)	1E14	Ohm	IEC 60093
電氣強度(Electric strength)	35	kV/mm	IEC 60243-1
相比漏電起痕指數(Comparative tracking index)	600	-	IEC 60112

其他屬性(Other properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
吸水率(Water absorption)	0.85	%	Sim. to ISO 62
吸濕性(Humidity absorption)	0.19	%	Sim. to ISO 62
密度(Density)	1570	kg/m3	ISO 1183

Test specimen production	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
Processing conditions acc. ISO	9990	-	ISO ....-2
Injection Molding, melt temperature	205	°C	ISO 294
Injection Molding, mold temperature	90	°C	ISO 10724
Injection Molding, injection velocity	200	mm/s	ISO 294
Injection Molding, pressure at hold	90	MPa	ISO 294

Diagrams 40 mm Water content 0,2%g. moisturizing is not necessary.DisclaimerCopyright M-Base Engineering+Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from M-Base; this is especially valid for claims of compensation resulting from consequential damages. M-Base explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.