流變性能(Rheological properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
熔體體積流動速率(Melt volume-flow rate) (MVR)	7.7	cm3/10min	ISO 1133
溫度(Temperature)	220	°C	ISO 1133
負載(Load)	2.16	kg	ISO 1133
成型收縮(Molding shrinkage) (parallel)	0.8	%	ISO 294-4, 2577
成型收縮(Molding shrinkage) (normal)	0.8	%	ISO 294-4, 2577

機械性能(機械性能(Mechanical properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	45	MPa	ISO 527-1/-2
Stress at 50% strain	6.5	MPa	ISO 527-1/-2
破壞時應變(Strain at break)	>50	%	ISO 527-1/-2
簡支梁沖擊強度(Charpy impact strength) (+23°C)	N	kJ/m2	ISO 179/1eU
簡支梁沖擊強度(Charpy impact strength) (-30°C)	N	kJ/m2	ISO 179/1eU
簡支梁缺口沖擊強度(Charpy notched impact strength) (+23°C)	N	kJ/m2	ISO 179/1eA
簡支梁缺口沖擊強度(Charpy notched impact strength) (-30°C)	N	kJ/m2	ISO 179/1eA
Stress at 10% elongation	3.2	MPa	ISO 527-1/-2
破壞時應變(Strain at break) TPE	>300	%	ISO 527-1/-2
破壞時應變(Stress at break) TPE	28	MPa	ISO 527-1/-2
抗拉強度(撕裂強度(Tear strength))	103	kN/m	ISO 34-1
Shore D hardness (15s)	34	-	ISO 868
ASTM數據(ASTM Data)
抗拉強度(Tensile Strength) at Break	20	MPa	ASTM D 638
斷裂伸長率(Elongation at Break)	700	%	ASTM D 638
彎曲彈性模量(彎曲彈性模量(Flexural Modulus))	55	MPa	ASTM D 790
Shore D Hardness	40	-	ASTM D 2240
懸臂梁式沖擊切口 (1/8 in)	N	kJ/m	ASTM D 256
懸臂梁式沖擊切口 (Low-溫度(Temperature))	N	kJ/m	ASTM D 256
溫度(Temperature)	-40	°C	ASTM D 256

熱性能(熱性能(Thermal properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
熔化溫度(熔化溫度(Melting temperature)) (10°C/min)	193	°C	ISO 11357-1/-3
玻璃化轉變溫度(Glass transition temperature) (10°C/min)	-50	°C	ISO 11357-1/-2
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	50	°C	ISO 75-1/-2
溫度負荷變形(Temp. of deflection under load) (0.45 MPa)	130	°C	ISO 75-1/-2
COEFF線性熱(Coeff. of linear therm. expansion) (parallel)	220	E-6/K	ISO 11359-1/-2
COEFF線性熱(Coeff. of linear therm. expansion) (normal)	190	E-6/K	ISO 11359-1/-2
燃燒性(球壓痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB	class	IEC 60695-11-10
厚度測試(Thickness tested)	1.5	mm	IEC 60695-11-10
UL 識別(recognition)	UL	-	-
燃燒性(球壓痕硬度(Burning behav)). at thickness h	HB	class	IEC 60695-11-10
厚度測試(Thickness tested)	3.0	mm	IEC 60695-11-10
UL 識別(recognition)	UL	-	-
Oxygen index	20	%	ISO 4589-1/-2
ASTM數據(ASTM Data)
UL 94 阻燃等級(Flame rating)	HB	-	UL 94
厚度測試(Thickness tested)	1.5	mm	-
熱膨脹系數(Coefficient of Thermal Expansion) (MD)	187	E-6/K	ASTM D 696
熱膨脹系數(Coefficient of Thermal Expansion) (TD)	219	E-6/K	ASTM D 696
DTUL @ 66 psi	55	°C	ASTM D 648
熔化溫度(Melting 溫度(Temperature))	193	°C	ASTM D 3418

電氣性能(Electrical properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
相對介電常數(Relative permittivity) (100Hz)	4.8	-	IEC 60250
相對介電常數(Relative permittivity) (1MHz)	4.7	-	IEC 60250
耗散因數(耗散因數(Dissipation factor)) (100Hz)	130	E-4	IEC 60250
耗散因數(耗散因數(Dissipation factor)) (1MHz)	130	E-4	IEC 60250
體積電阻率(Volume resistivity)	4E10	Ohm*m	IEC 60093
表面電阻率(Surface resistivity)	3E14	Ohm	IEC 60093
電氣強度(Electric strength)	18	kV/mm	IEC 60243-1
相比漏電起痕指數(Comparative tracking index)	600	-	IEC 60112

流變計算屬性(Rheological calculation properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
密度(Density) of melt	1100	kg/m3	-

Diagrams ISO 1817 Liquid C) (23°C)

ISO 1817 Liquid 4) (23°C)

ISO 1817 Liquid F) (23°C)

ISO 1817 Liquid F) (90°C)

ISO 1817 Liquid F) (>90°C)

Salt solutions

4 Brake fluid (130°C)

Hytrel? 4069|TPC|DuPont