填料/增強材料: 玻璃\礦物, 30% 填料按重量
特性: 低翹曲性,良好的流動性,收縮性低
加工方法: 注射成型
多點數據: Coefficient of Thermal Expansion vs. Temperature (ASTM E831),Elastic Modulus vs Temperature (ASTM D4065),Flexural DMA (ASTM D4065),Instrumented Impact (Energy) (ASTM D3763),Instrumented Impact (Load) (ASTM D3763),Pressure-Volume-Temperature (PVT - Zoller Method),Shear DMA (ASTM D4065),Specific Heat vs. Temperature (ASTM D3417),Tensile Creep (ASTM D2990),Tensile Fatigue,Tensile Stress vs. Strain (ASTM D638),Thermal Conductivity vs. Temperature (ASTM E1530),Viscosity vs. Shear Rate (ASTM D3835)
- 料筒前部溫度 °C
- 排氣孔深度 mm
- 特定體積 0.663 cm3/g ASTM D792
- 伸長率 2.0 % ASTM D638
- 背壓 MPa
- 干燥溫度 121 °C
- 建議的最大水分含量 0.020 %
- 干燥溫度 121 °C
- 線形熱膨脹系數 - 流動 ASTM E831
- 排氣孔深度 mm