Availability
|
|
|
Filler / Reinforcement
|
|
|
Forms
|
|
| Physical | Dry | Conditioned |
Unit
|
Test Method
|
|
Density
|
1.23
|
--
|
g/cm³
|
ISO 1183 |
|
Molding Shrinkage - Flow
|
0.50
|
--
|
%
|
ISO 294-4 |
|
Water Absorption
|
ISO 62 | |||
|
Saturation, 23°C
|
7.2
|
--
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
2.1
|
--
|
%
|
| Mechanical | Dry | Conditioned |
Unit
|
Test Method
|
|
Tensile Modulus
|
ISO 527-2 | |||
|
23°C
|
6300
|
4500
|
MPa
|
|
|
90°C
|
3100
|
--
|
MPa
|
|
|
120°C
|
2600
|
--
|
MPa
|
|
|
Tensile Stress
|
ISO 527-2 | |||
|
Break, 23°C
|
130
|
80.0
|
MPa
|
|
|
Break, 90°C
|
60.0
|
--
|
MPa
|
|
|
Break, 120°C
|
50.0
|
--
|
MPa
|
|
|
Tensile Strain (Break, 23°C)
|
3.0
|
4.0
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
ISO 178 | |||
|
23°C
|
5500
|
3900
|
MPa
|
|
|
90°C
|
2800
|
--
|
MPa
|
|
|
Flexural Strength
|
ISO 178 | |||
|
23°C
|
170
|
120
|
MPa
|
|
|
90°C
|
85.0
|
--
|
MPa
|
|
| Impact | Dry | Conditioned |
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179 | |||
|
-30°C
|
5.0
|
--
|
kJ/m²
|
|
|
23°C
|
8.0
|
20
|
kJ/m²
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179 | |||
|
-30°C
|
20
|
--
|
kJ/m²
|
|
|
23°C
|
25
|
40
|
kJ/m²
|
| Thermal | Dry | Conditioned |
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
||||
|
0.45 MPa, Unannealed
|
255
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
245
|
--
|
°C
|
ISO 75-2/A |
|
CLTE - Flow (23°C)
|
0.000036
|
--
|
cm/cm/°C
|
ISO 11359-2 |
|
Thermal Conductivity
|
0.25
|
--
|
W/m/K
|
ISO 8302 |
| Electrical | Dry | Conditioned |
Unit
|
Test Method
|
|
Surface Resistivity
|
1.0E+12
|
--
|
ohm
|
ASTM D257 |
|
Electric Strength (2.00 mm)
|
35
|
30
|
kV/mm
|
IEC 60243-1 |
|
Comparative Tracking Index
|
500
|
500
|
V
|
IEC 60112 |
| Flammability | Dry | Conditioned |
Unit
|
Test Method
|
|
Flame Rating (1.60 mm)
|
HB
|
--
|
|
UL 94 |
| Additional Information | ||||
|
Dry
|
The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods.
The value listed as Coefficient of Linear Thermal Expansion, Flow ISO 11359-1-2, was tested in accordance with ISO 7991. |
|||