Availability
|
|
|
Filler / Reinforcement
|
|
|
Forms
|
|
| Physical | Dry | Conditioned |
Unit
|
Test Method
|
|
Density
|
1.23
|
--
|
g/cm³
|
ISO 1183 |
|
Molding Shrinkage - Flow
|
0.30
|
--
|
%
|
ISO 294-4 |
|
Water Absorption
|
ISO 62 | |||
|
Saturation, 23°C
|
6.8
|
--
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
2.0
|
--
|
%
|
| Mechanical | Dry | Conditioned |
Unit
|
Test Method
|
|
Tensile Modulus
|
ISO 527-2 | |||
|
23°C
|
16000
|
11000
|
MPa
|
|
|
90°C
|
9500
|
--
|
MPa
|
|
|
120°C
|
7000
|
--
|
MPa
|
|
|
Tensile Stress
|
ISO 527-2 | |||
|
Break, 23°C
|
240
|
180
|
MPa
|
|
|
Break, 90°C
|
130
|
--
|
MPa
|
|
|
Break, 120°C
|
110
|
--
|
MPa
|
|
|
Tensile Strain (Break, 23°C)
|
3.0
|
6.0
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
ISO 178 | |||
|
23°C
|
14000
|
10500
|
MPa
|
|
|
90°C
|
8500
|
--
|
MPa
|
|
|
Flexural Strength
|
ISO 178 | |||
|
23°C
|
330
|
230
|
MPa
|
|
|
90°C
|
180
|
--
|
MPa
|
|
| Impact | Dry | Conditioned |
Unit
|
Test Method
|
|
Charpy Notched Impact Strength (23°C)
|
9.0
|
16
|
kJ/m²
|
ISO 179 |
|
Charpy Unnotched Impact Strength (23°C)
|
35
|
55
|
kJ/m²
|
ISO 179 |
| Thermal | Dry | Conditioned |
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
||||
|
0.45 MPa, Unannealed
|
255
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
250
|
--
|
°C
|
ISO 75-2/A |
|
CLTE - Flow (23°C)
|
0.000026
|
--
|
cm/cm/°C
|
ISO 11359-2 |
|
Thermal Conductivity
|
0.47
|
--
|
W/m/K
|
ISO 8302 |
| Electrical | Dry | Conditioned |
Unit
|
Test Method
|
|
Surface Resistivity
|
1.0E+3
|
--
|
ohm
|
ASTM D257 |
| Flammability | Dry | Conditioned |
Unit
|
Test Method
|
|
Flame Rating (1.60 mm)
|
HB
|
--
|
|
UL 94 |
| Additional Information | ||||
|
Dry
|
The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods.
The value listed as Coefficient of Linear Thermal Expansion, Flow ISO 11359-1-2, was tested in accordance with ISO 7991. Wear Factor, ASTM D3702, 23°C: 38 Static c.o.f., ASTM D3702, 23°C: 0.18 Dynamic c.o.f., ASTM D3702, 23°C: 0.21 |
|||