| Physical | Dry | Conditioned |
Unit
|
Test Method
|
|
Density
|
1.28
|
--
|
g/cm³
|
ISO 1183 |
|
Molding Shrinkage
|
ISO 294-4 | |||
|
Across Flow
|
1.2
|
--
|
%
|
|
|
Flow
|
0.70
|
--
|
%
|
|
|
Water Absorption
|
ISO 62 | |||
|
Saturation, 23°C
|
7.0
|
--
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
2.0
|
--
|
%
|
| Mechanical | Dry | Conditioned |
Unit
|
Test Method
|
|
Tensile Modulus
|
7400
|
5600
|
MPa
|
ISO 527-2 |
|
Tensile Stress (Break)
|
130
|
90.0
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Break)
|
3.0
|
5.5
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
6800
|
--
|
MPa
|
ISO 178 |
|
Flexural Strength
|
215
|
--
|
MPa
|
ISO 178 |
| Impact | Dry | Conditioned |
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
|
-30°C
|
4.0
|
4.0
|
kJ/m²
|
|
|
23°C
|
6.0
|
10
|
kJ/m²
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | |||
|
-30°C
|
40
|
40
|
kJ/m²
|
|
|
23°C
|
40
|
70
|
kJ/m²
|
| Thermal | Dry | Conditioned |
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
||||
|
0.45 MPa, Unannealed
|
250
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
235
|
--
|
°C
|
ISO 75-2/A |
|
Melting Temperature 2
|
260
|
--
|
°C
|
ISO 11357-3 |
|
CLTE
|
ISO 11359-2 | |||
|
Flow
|
0.000020
|
--
|
cm/cm/°C
|
|
|
Transverse
|
0.000080
|
--
|
cm/cm/°C
|
| Electrical | Dry | Conditioned |
Unit
|
Test Method
|
|
Surface Resistivity
|
--
|
1.0E+14
|
ohm
|
IEC 60093 |
|
Volume Resistivity
|
1.0E+15
|
1.0E+13
|
ohm·cm
|
IEC 60093 |
|
Electric Strength
|
35
|
30
|
kV/mm
|
IEC 60243-1 |
|
Relative Permittivity
|
IEC 60250 | |||
|
100 Hz
|
3.70
|
11.0
|
|
|
|
1 MHz
|
3.30
|
4.60
|
|
|
|
Dissipation Factor
|
IEC 60250 | |||
|
100 Hz
|
0.011
|
0.14
|
|
|
|
1 MHz
|
0.018
|
0.10
|
|
|
| Flammability | Dry | Conditioned |
Unit
|
Test Method
|
|
Flammability Classification
|
IEC 60695-11-10, -20 | |||
|
0.710 mm
|
HB
|
--
|
|
|
|
1.50 mm
|
HB
|
--
|
|