Availability
|
|
|||
|
Filler / Reinforcement
|
|
|||
|
Features
|
|
|||
|
Uses
|
|
|||
|
Appearance
|
|
|||
|
Resin ID (ISO 1043)
|
|
| Physical | Dry | Conditioned |
Unit
|
Test Method
|
|
Density (23°C)
|
1.24
|
--
|
g/cm³
|
ISO 1183 |
|
Spiral Flow 2, 3
|
99.0
|
--
|
cm
|
Internal Method |
|
Molding Shrinkage
|
ISO 294-4 | |||
|
Across Flow
|
1.4
|
--
|
%
|
|
|
Flow
|
0.40
|
--
|
%
|
|
|
Water Absorption (Saturation, 23°C)
|
6.7 to 7.3
|
--
|
%
|
ISO 62 |
|
Humidity Absorption - 62% RH (70°C)
|
2.5 to 2.7
|
--
|
%
|
ISO 1110 |
| Hardness | Dry | Conditioned |
Unit
|
Test Method
|
|
Ball Indentation Hardness (H 961/30)
|
200
|
--
|
MPa
|
ISO 2039-1 |
| Mechanical | Dry | Conditioned |
Unit
|
Test Method
|
|
Tensile Modulus
|
6400
|
3700
|
MPa
|
ISO 527-2/1 |
|
Tensile Stress (Break)
|
140
|
80.0
|
MPa
|
ISO 527-2/5 |
|
Tensile Strain (Break)
|
3.5
|
12
|
%
|
ISO 527-2/5 |
|
Flexural Modulus 4
|
6100
|
--
|
MPa
|
ISO 178 |
|
Flexural Strength 4
|
200
|
--
|
MPa
|
ISO 178 |
| Impact | Dry | Conditioned |
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
|
-30°C
|
6.0
|
--
|
kJ/m²
|
|
|
23°C
|
7.0
|
8.0
|
kJ/m²
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | |||
|
-30°C
|
43
|
--
|
kJ/m²
|
|
|
23°C
|
45
|
88
|
kJ/m²
|
| Thermal | Dry | Conditioned |
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
||||
|
0.45 MPa, Unannealed
|
260
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
245
|
--
|
°C
|
ISO 75-2/A |
|
Melting Temperature 5
|
262
|
--
|
°C
|
DIN EN 11357-1 |
|
CLTE
|
ISO 11359-2 | |||
|
Flow: 23 to 80°C
|
0.000034
|
--
|
cm/cm/°C
|
|
|
Transverse: 23 to 80°C
|
0.00011
|
--
|
cm/cm/°C
|
| Electrical | Dry | Conditioned |
Unit
|
Test Method
|
|
Surface Resistivity
|
1.0E+12
|
--
|
ohm
|
IEC 60093 |
|
Volume Resistivity
|
1.0E+13
|
--
|
ohm·cm
|
IEC 60093 |
|
Comparative Tracking Index (Solution A)
|
600
|
--
|
V
|
IEC 60112 |
| Flammability | Dry | Conditioned |
Unit
|
Test Method
|
|
Burning Rate 6 (1.00 mm)
|
< 100
|
--
|
mm/min
|
FMVSS 302 |
|
Flame Rating (1.60 mm)
|
HB
|
--
|
|
UL 94 |
|
Glow Wire Flammability Index (1.60 mm)
|
650
|
--
|
°C
|
IEC 60695-2-12 |
| Additional Information | Dry | Conditioned |
Unit
|
Test Method
|
|
Reinforcement Content
|
15
|
--
|
%
|
ISO 1172 |