Availability
|
|
|||
|
Features
|
|
|||
|
Forms
|
|
|||
|
Processing Method
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
1.08
|
g/cm³
|
ISO 1183 |
|
Molding Shrinkage
|
1.0 to 2.0
|
%
|
Internal Method |
|
Water Absorption (23°C, 24 hr)
|
0.80
|
%
|
ISO 62 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Stress (Yield)
|
80.0
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Break)
|
120
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
2000
|
MPa
|
ISO 178 |
|
Flexural Strength
|
110
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact Strength (23°C)
|
15
|
kJ/m²
|
ISO 180 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
|||
|
0.45 MPa, Unannealed
|
200
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
61.0
|
°C
|
ISO 75-2/A |
| Flammability |
Nominal Value
|
|
Test Method
|
|
Flame Rating
|
HB
|
|
UL 94 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
80.0 to 100
|
°C
|
|
|
Drying Time
|
4.0 to 6.0
|
hr
|
|
|
Rear Temperature
|
250 to 280
|
°C
|
|
|
Middle Temperature
|
240 to 270
|
°C
|
|
|
Front Temperature
|
240 to 260
|
°C
|
|
|
Nozzle Temperature
|
250 to 280
|
°C
|
|
|
Mold Temperature
|
50.0 to 110
|
°C
|
|
|
Injection Pressure
|
30.0 to 80.0
|
MPa
|
|
|
Holding Pressure
|
40.0 to 50.0
|
MPa
|
|
|
Back Pressure
|
5.00 to 10.0
|
MPa
|
|
|
Screw Speed
|
40 to 70
|
rpm
|
|
| Injection Notes | |||
|
Cylinder Temperature 4: 240 to 260°C
|
|||