特點：
1、綜合性能較好，沖擊強度較高，化學穩定性，電性能良好.
2、與372有機玻璃的熔接性良好，制成雙色塑件，且可表面鍍鉻，噴漆處理.
3、有高抗沖、高耐熱、阻燃、增強、透明等級別。
4、流動性比HIPS差一點，比PMMA、PC等好，柔韌性好。
5、用途：適于制作一般機械零件，減磨耐磨零件，傳動零件和電訊零件.
6、同PVC（聚氯乙烯）一樣在屈折處會出現白化現象。
?
典型應用范Χ:
汽車內外飾：儀表板，飾柱，儀表前蓋，格柵，內外飾件 2.商務設備機殼和內置部件：筆記本/臺式電腦，復印機，打印機，繪圖儀，顯示器 3.電信，移動電話外殼，附件以及智能卡（SIM卡）： 4.電器產品，電子產品外殼，電表罩和殼體，家用開關，插頭和插座，電纜電線管道 5.家用電器，如洗衣機，吹風機，微波¯內外部件等。
?
| ?物性表： | |||||
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity? | 1.14?g/cc | 1.14?g/cc | ASTM D792 | ||
| Density? | 1.14?g/cc | 0.0412?lb/in3 | ISO 1183 | ||
| Moisture Absorption? | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 | ||
| Water Absorption at Saturation? | 0.40 % | 0.40 % | ISO 62 | ||
| Viscosity? | 195000?cP | 195000?cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 | ||
| Linear Mold Shrinkage, Flow? | 0.0050?-?0.0070?cm/cm @Thickness 3.20 mm |
0.0050?-?0.0070?in/in @Thickness 0.126 in |
SABIC Method | ||
| Linear Mold Shrinkage, Transverse? | 0.0050?-?0.0070?cm/cm @Thickness 3.20 mm |
0.0050?-?0.0070?in/in @Thickness 0.126 in |
SABIC Method | ||
| Melt Flow? | 22?g/10 min @Load 5.00 kg, Temperature 260 °C |
22?g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 | ||
| Melt Index of Compound? | 21?g/10 min @Load 5.00 kg, Temperature 260 °C |
21?g/10 min @Load 11.0 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 | ||
| ? | |||||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break? | 51.0?MPa | 7400?psi | 50 mm/min; ISO 527 | ||
| ? | 52.0?MPa | 7540?psi | Type I, 50 mm/min; ASTM D638 | ||
| Tensile Strength, Yield? | 54.0?MPa | 7830?psi | 50 mm/min; ISO 527 | ||
| ? | 55.0?MPa | 7980?psi | Type I, 50 mm/min; ASTM D638 | ||
| Elongation at Break? | 115 % | 115 % | Type I, 50 mm/min; ASTM D638 | ||
| ? | 115 % | 115 % | 50 mm/min; ISO 527 | ||
| Elongation at Yield? | 4.5 % | 4.5 % | 50 mm/min; ISO 527 | ||
| ? | 4.7 % | 4.7 % | Type I, 50 mm/min; ASTM D638 | ||
| Tensile Modulus? | 2.20?GPa | 319?ksi | 1 mm/min; ISO 527 | ||
| ? | 2.30?GPa | 334?ksi | 5 mm/min; ASTM D638 | ||
| Flexural Yield Strength? | 83.0?MPa | 12000?psi | 2 mm/min; ISO 178 | ||
| ? | 89.0?MPa | 12900?psi | 1.3 mm/min, 50 mm span; ASTM D790 | ||
| Flexural Modulus? | 2.20?GPa | 319?ksi | 2 mm/min; ISO 178 | ||
| ? | 2.30?GPa | 334?ksi | 1.3 mm/min, 50 mm span; ASTM D790 | ||
| Izod Impact, Notched? | 6.40?J/cm | 12.0?ft-lb/in | ASTM D256 | ||
| ?? | 4.80?J/cm @Temperature -30.0 °C |
8.99?ft-lb/in @Temperature -22.0 °F |
ASTM D256 | ||
| Izod Impact, Notched (ISO)? | 70.0?kJ/m2 | 33.3?ft-lb/in2 | 80*10*3; ISO 180/1A | ||
| ?? | 45.0?kJ/m2 @Temperature -30.0 °C |
21.4?ft-lb/in2 @Temperature -22.0 °F |
80*10*3; ISO 180/1A | ||
| Charpy Impact, Notched? | 7.00?J/cm2 | 33.3?ft-lb/in2 | Edgew 80*10*3 sp=62mm; ISO 179/1eA | ||
| ?? | 4.50?J/cm2 @Temperature -30.0 °C |
21.4?ft-lb/in2 @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eA | ||
| Dart Drop, Total Energy ?? | 56.0?J @Temperature 23.0 °C |
41.3?ft-lb @Temperature 73.4 °F |
ASTM D3763 | ||
| ? | 70.0?J @Temperature -30.0 °C |
51.6?ft-lb @Temperature -22.0 °F |
ASTM D3763 | ||
| ? | |||||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity? | >=?1.00e+15?ohm-cm | >=?1.00e+15?ohm-cm | IEC 60093 | ||
| Surface Resistance? | >=?1.00e+15?ohm | >=?1.00e+15?ohm | ROA; IEC 60093 | ||
| Dielectric Strength ??? | 17.0?kV/mm @Thickness 3.20 mm |
432?kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 | ||
| ? | 25.0?kV/mm @Thickness 1.60 mm |
635?kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | ||
| ? | 35.0?kV/mm @Thickness 0.800 mm |
889?kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | ||
| ? | |||||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow ?? | 70.0?μm/m-°C @Temperature -40.0 - 40.0 °C |
38.9?μin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | ||
| ? | 80.0?μm/m-°C @Temperature -40.0 - 40.0 °C |
44.4?μin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | ||
| CTE, linear, Transverse to Flow ??? | 70.0?μm/m-°C @Temperature -40.0 - 40.0 °C |
38.9?μin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | ||
| ? | 80.0?μm/m-°C @Temperature -40.0 - 40.0 °C |
44.4?μin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | ||
| Thermal Conductivity? | 0.200?W/m-K | 1.39?BTU-in/hr-ft2-°F | ISO 8302 | ||
| Deflection Temperature at 0.46 MPa (66 psi)? | 126?°C | 259?°F | Flatw 80*10*4 sp=64mm; ISO 75/Bf | ||
| Deflection Temperature at 1.8 MPa (264 psi)? | 105?°C | 221?°F | Flatw 80*10*4 sp=64mm; ISO 75/Af | ||
| ? | 107?°C @Thickness 3.20 mm |
225?°F @Thickness 0.126 in |
unannealed; ASTM D648 | ||
| Vicat Softening Point? | 127?°C | 261?°F | Rate B/50; ASTM D1525 | ||
| ? | 127?°C | 261?°F | Rate B/50; ISO 306 | ||
| ? | 129?°C | 264?°F | Rate B/120; ISO 306 | ||
| UL RTI, Electrical? | 60.0?°C | 140?°F | UL 746B | ||
| UL RTI, Mechanical with Impact? | 60.0?°C | 140?°F | UL 746B | ||
| UL RTI, Mechanical without Impact? | 60.0?°C | 140?°F | UL 746B | ||
| Flammability, UL94 ?? | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 | ||
| ? | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
UL 94 | ||
| Glow Wire Test? | 750?°C | 1380?°F | IEC 60695-2-13 | ||
| ? | |||||
| De |
|||||
| Ball Pressure Test, 75°C +/- 2°C | Pass | IEC 60695-10-2 |
|||
供應原料，品質真實,物實價廉。