特點：
1、綜合性能較好，沖擊強度較高，化學穩定性，電性能良好.
2、與372有機玻璃的熔接性良好，制成雙色塑件，且可表面鍍鉻，噴漆處理.
3、有高抗沖、高耐熱、阻燃、增強、透明等級別。
4、流動性比HIPS差一點，比PMMA、PC等好，柔韌性好。
5、用途：適于制作一般機械零件，減磨耐磨零件，傳動零件和電訊零件.
6、同PVC（聚氯乙烯）一樣在屈折處會出現白化現象。
?
典型應用范Χ:
汽車內外飾：儀表板，飾柱，儀表前蓋，格柵，內外飾件 2.商務設備機殼和內置部件：筆記本/臺式電腦，復印機，打印機，繪圖儀，顯示器 3.電信，移動電話外殼，附件以及智能卡（SIM卡）： 4.電器產品，電子產品外殼，電表罩和殼體，家用開關，插頭和插座，電纜電線管道 5.家用電器，如洗衣機，吹風機，微波¯內外部件等。
| ?物性表： | |||||
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity? | 1.15?g/cc | 1.15?g/cc | ASTM D792 | ||
| Density? | 1.15?g/cc | 0.0415?lb/in3 | ISO 1183 | ||
| Moisture Absorption? | 0.160 % | 0.160 % | 23°C / 50% RH; ISO 62 | ||
| Water Absorption at Saturation? | 0.60 % | 0.60 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow? | 0.0040?-?0.0060?cm/cm @Thickness 3.20 mm |
0.0040?-?0.0060?in/in @Thickness 0.126 in |
SABIC Method | ||
| Melt Flow? | 22?g/10 min @Load 5.00 kg, Temperature 260 °C |
22?g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 | ||
| Melt Index of Compound? | 20?g/10 min @Load 5.00 kg, Temperature 260 °C |
20?g/10 min @Load 11.0 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 | ||
| ? | |||||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell L? | 90 | 90 | ISO 2039-2 | ||
| Tensile Strength at Break? | 45.0?MPa | 6530?psi | Type I, 50 mm/min; ASTM D638 | ||
| ? | 45.0?MPa | 6530?psi | 5 mm/min; ISO 527 | ||
| ? | 45.0?MPa | 6530?psi | 50 mm/min; ISO 527 | ||
| Tensile Strength, Yield? | 45.0?MPa | 6530?psi | 5 mm/min; ISO 527 | ||
| ? | 50.0?MPa | 7250?psi | 50 mm/min; ISO 527 | ||
| ? | 50.0?MPa | 7250?psi | Type I, 50 mm/min; ASTM D638 | ||
| Elongation at Break? | 45 % | 45 % | Type I, 50 mm/min; ASTM D638 | ||
| ? | 50 % | 50 % | 50 mm/min; ISO 527 | ||
| ? | 60 % | 60 % | 5 mm/min; ISO 527 | ||
| Elongation at Yield? | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 | ||
| ? | 5.0 % | 5.0 % | 5 mm/min; ISO 527 | ||
| ? | 5.0 % | 5.0 % | 50 mm/min; ISO 527 | ||
| Tensile Modulus? | 2.40?GPa | 348?ksi | 5 mm/min; ASTM D638 | ||
| ? | 2.40?GPa | 348?ksi | 1 mm/min; ISO 527 | ||
| Flexural Yield Strength? | 80.0?MPa | 11600?psi | 1.3 mm/min, 50 mm span; ASTM D790 | ||
| ? | 80.0?MPa | 11600?psi | 2 mm/min; ISO 178 | ||
| Flexural Modulus? | 2.30?GPa | 334?ksi | 1.3 mm/min, 50 mm span; ASTM D790 | ||
| ? | 2.30?GPa | 334?ksi | 2 mm/min; ISO 178 | ||
| Izod Impact, Notched? | 1.00?J/cm | 1.87?ft-lb/in | Izod Impact, double-gated, 23°C; SABIC Method | ||
| ? | 4.50?J/cm | 8.43?ft-lb/in | ASTM D256 | ||
| ?? | 2.50?J/cm @Temperature -30.0 °C |
4.68?ft-lb/in @Temperature -22.0 °F |
ASTM D256 | ||
| Izod Impact, Notched (ISO)? | 40.0?kJ/m2 | 19.0?ft-lb/in2 | 80*10*3; ISO 180/1A | ||
| ?? | 20.0?kJ/m2 @Temperature -30.0 °C |
9.52?ft-lb/in2 @Temperature -22.0 °F |
80*10*3; ISO 180/1A | ||
| Charpy Impact, Notched? | 4.00?J/cm2 | 19.0?ft-lb/in2 | Edgew 80*10*3 sp=62mm; ISO 179/1eA | ||
| ?? | 2.00?J/cm2 @Temperature -30.0 °C |
9.52?ft-lb/in2 @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eA | ||
| Dart Drop, Total Energy ?? | 25.0?J @Temperature -30.0 °C |
18.4?ft-lb @Temperature -22.0 °F |
ASTM D3763 | ||
| ? | 55.0?J @Temperature 23.0 °C |
40.6?ft-lb @Temperature 73.4 °F |
ASTM D3763 | ||
| Impact Test? | 70.0?J | 51.6?ft-lb | Multiaxial Impact; ISO 6603 | ||
| Taber Abrasion, mg/1000 Cycles? | 70 | 70 | CS-17, 1 kg; SABIC Method | ||
| ? | |||||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity? | >=?1.00e+15?ohm-cm | >=?1.00e+15?ohm-cm | ASTM D257 | ||
| Surface Resistance? | >=?1.00e+15?ohm | >=?1.00e+15?ohm | ASTM D257 | ||
| Dielectric Constant ?? | 2.7 @Frequency 1.00e+6 Hz |
2.7 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| ? | 2.9 @Frequency 50.0 - 60.0 Hz |
2.9 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | ||
| Dielectric Strength ?? | 27.0?kV/mm @Thickness 1.60 mm |
686?kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | ||
| ? | 36.0?kV/mm @Thickness 0.800 mm |
914?kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | ||
| Dissipation Factor ?? | 0.010 @Frequency 50.0 - 60.0 Hz |
0.010 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | ||
| ? | 0.011 @Frequency 1.00e+6 Hz |
0.011 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| ? | |||||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow ?? | 71.0?μm/m-°C @Temperature -40.0 - 40.0 °C |
39.4?μin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | ||
| ? | 75.0?μm/m-°C @Temperature -40.0 - 40.0 °C |
41.7?μin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | ||
| CTE, linear, Transverse to Flow ?? | 73.0?μm/m-°C @Temperature -40.0 - 40.0 °C |
40.6?μin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | ||
| ? | 77.0?μm/m-°C @Temperature -40.0 - 40.0 °C |
42.8?μin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | ||
| Thermal Conductivity? | 0.200?W/m-K | 1.39?BTU-in/hr-ft2-°F | ASTM C177 | ||
| ? | 0.200?W/m-K | 1.39?BTU-in/hr-ft2-°F | ISO 8302 | ||
| Hot Ball Pressure Test? | <=?100?°C | <=?212?°F | IEC 60695-10-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi)? | 117?°C | 243?°F | Edgew 120*10*4 sp=100mm; ISO 75/Be | ||
| ? | 115?°C @Thickness 3.20 mm |
239?°F @Thickness 0.126 in |
unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi)? | 95.0?°C | 203?°F | Edgew 120*10*4 sp=100mm; ISO 75/Ae | ||
| ? | 95.0?°C @Thickness 3.20 mm |
203?°F @Thickness 0.126 in |
unannealed; ASTM D648 | ||
| Vicat Softening Point? | 113?°C | 235?°F | Rate B/50; ASTM D1525 | ||
| ? | 114?°C | 237?°F | Rate B/50; ISO 306 | ||
| ? | 116?°C | 241?°F | Rate B/120; ISO 306 | ||
| UL RTI, Electrical? | 60.0?°C | 140?°F | UL 746B | ||
| UL RTI, Mechanical with Impact? | 60.0?°C | 140?°F | UL 746B | ||
| UL RTI, Mechanical without Impact? | 60.0?°C | 140?°F | UL 746B | ||
| Flammability, UL94?? | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
UL 94 | ||
| ? | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
UL 94 | ||
| Glow Wire Test? | 650?°C @Thickness 3.20 mm |
1200?°F @Thickness 0.126 in |
IEC 60695-2-12 | ||
| ? | |||||
| De |
|||||
| Ball Pressure Test, 75°C +/- 2°C | passes | IEC 60695-10-2 |
|||