| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Test | 111 cm³/g | 111 cm³/g | Viscosity number | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM Data; MD | ||
| Melt Flow | 22 g/10 min @Load 2.16 kg, Temperature 250 °C |
22 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 93.0 MPa | 13500 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 93.0 MPa | 13500 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 4.0 % | 4.0 % | 0.2 in/min; ASTM Test | ||
| 4.0 % | 4.0 % | 5mm/min; ISO 527 | |||
| Tensile Modulus | 5.52 GPa | 801 ksi | ASTM Test | ||
| 6.00 GPa | 870 ksi | 1mm/min; ISO 527 | |||
| Flexural Modulus | 4.80 GPa | 696 ksi | ISO Data | ||
| 4.83 GPa | 701 ksi | ASTM Test | |||
| Izod Impact, Notched | 0.430 J/cm @Temperature -40.0 °C |
0.806 ft-lb/in @Temperature -40.0 °F |
ASTM Test | ||
| 0.530 J/cm @Thickness 3.17 mm |
0.993 ft-lb/in @Thickness 0.125 in |
ASTM Test | |||
| Izod Impact, Notched (ISO) | 8.50 kJ/m² | 4.04 ft-lb/in² | ISO Test | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
Dielectric Constant  |
3.7 @Frequency 100 Hz |
3.7 @Frequency 100 Hz |
IEC 60250 | ||
| 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Dissipation Factor |
0.0012 @Frequency 100 Hz |
0.0012 @Frequency 100 Hz |
IEC 60250 | ||
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ISO 11359 | ||
| Melting Point | 223 °C | 433 °F | 10 K/min | ||
| 223 °C | 433 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 183 °C | 361 °F | ISO 75 | ||
| 203 °C | 397 °F | ASTM Test | |||
| Flammability, UL94 |
HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|||
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 265 °C | 509 °F | Injection molding | ||
| Injection Velocity | 70.0 mm/sec | 2.76 in/sec | Injection molding | ||
| De |
|||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| NSF Std. 61 | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| Light stabilized or stable to light | |||||
| Lubricant | |||||
| U.V. stabilized or stable to weather | |||||
圖：
上海松翰塑化科技有限公司！本公司承諾，假一賠百！所有產(chǎn)品都是原廠家，原包裝一線獨家營銷！
我司所銷售所有產(chǎn)品均為原廠原包，均可提供相關(guān)資料報告（如：物性表，MSDS報告，UL報告，COA報告，SGS報告，F(xiàn)DA等）！
歡迎新老客戶來電或QQ咨詢：
聯(lián)系人：李先生
聯(lián)系電話；13636696005
聯(lián)系QQ；1020580970
聯(lián)系郵箱；1020580970@qq.com