PA66-I 444AHS BK152 材料說明：增韌，熱穩定，聚酰胺66
PA66-I 444AHS BK152 性能表：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | DAM; ISO 1183 | ||
| Water Absorption | 1.30 % @Time 86400 sec |
1.30 % @Time 24.0 hour |
DAM; ASTM D 570 | ||
| 1.30 % @Thickness 2.00 mm |
1.30 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 50%RH; ISO 527-1/-2 | ||
| 62.0 MPa | 8990 psi | DAM; ISO 527-1/-2 | |||
| Elongation at Break | 25.0 % | 25.0 % | Nominal; DAM; ISO 527-1/-2 | ||
| >= 50.0 % | >= 50.0 % | Nominal; 50%RH; ISO 527-1/-2 | |||
| Elongation at Yield | 5.50 % | 5.50 % | DAM; ISO 527-1/-2 | ||
| 15.0 % | 15.0 % | 50%RH; ISO 527-1/-2 | |||
| Tensile Modulus | 1.10 GPa | 160 ksi | 50%RH; ISO 527-1/-2 | ||
| 2.40 GPa | 348 ksi | DAM; ISO 527-1/-2 | |||
| 0.274 GPa @Temperature 150 °C |
39.7 ksi @Temperature 302 °F |
50%RH; ISO 11403-1,-2 | |||
| 0.329 GPa @Temperature 150 °C |
47.7 ksi @Temperature 302 °F |
DAM; ISO 11403-1,-2 | |||
| 0.391 GPa @Temperature 90.0 °C |
56.7 ksi @Temperature 194 °F |
50%RH; ISO 11403-1,-2 | |||
| 0.450 GPa @Temperature 90.0 °C |
65.3 ksi @Temperature 194 °F |
DAM; ISO 11403-1,-2 | |||
| 1.134 GPa @Temperature 23.0 °C |
164.5 ksi @Temperature 73.4 °F |
50%RH; ISO 11403-1,-2 | |||
| 2.412 GPa @Temperature 0.000 °C |
349.8 ksi @Temperature 32.0 °F |
50%RH; ISO 11403-1,-2 | |||
| 2.426 GPa @Temperature 23.0 °C |
351.9 ksi @Temperature 73.4 °F |
DAM; ISO 11403-1,-2 | |||
| 2.522 GPa @Temperature 0.000 °C |
365.8 ksi @Temperature 32.0 °F |
DAM; ISO 11403-1,-2 | |||
| 2.992 GPa @Temperature -40.0 °C |
434.0 ksi @Temperature -40.0 °F |
DAM; ISO 11403-1,-2 | |||
| 3.177 GPa @Temperature -40.0 °C |
460.8 ksi @Temperature -40.0 °F |
50%RH; ISO 11403-1,-2 | |||
| Flexural Modulus | 2.27 GPa | 329 ksi | DAM; ISO 178 | ||
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -40.0 °C |
4.76 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 180/1A | ||
| 16.0 kJ/m² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | DAM; ISO 11359-1/-2 | ||
| Melting Point | 260 °C | 500 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | >= 280 °C | >= 536 °F | |||
| 290 °C | 554 °F | Optimum | |||
| <= 300 °C | <= 572 °F | ||||
| Mold Temperature | >= 50.0 °C | >= 122 °F | |||
| 70.0 °C | 158 °F | Optimum | |||
| <= 90.0 °C | <= 194 °F | ||||
| Ejection Temperature | 190 °C | 374 °F | |||
| Drying Temperature | 80.0 °C @Time 7200 - 14400 sec |
176 °F @Time 2.00 - 4.00 hour |
|||
| Moisture Content | 0.200 % | 0.200 % | |||
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi | |||
| De |
|||||
| Delivery form | Pellets | ||||
| Drying Recommended | yes | ||||
| Hold pressure time | 4 s/mm | ||||
| Max. screw tangential speed (m/s) | 0.3 | DAM | |||
| Part Marking Code | >PA66-I< | ISO 11469 | |||
| Processing | Injection Molding | ||||
| Regional Availability | North America | ||||
| South and Central America | |||||
| Resin Identification | PA66-I | ISO 1043 | |||
| Special characteristics | Heat stabilized or stable to heat | ||||