| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.35 % | 0.35 % | Test Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C/50% R.H.; Test Sim. to ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0013 cm/cm | 0.0013 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0012 cm/cm | 0.0012 in/in | ISO 294-4, 2577 | ||
| Melt Flow | 19 g/10 min @Load 2.16 kg, Temperature 260 °C |
19 g/10 min @Load 4.76 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527-1/-2 | ||
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527-1/-2 | ||
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-1/-2 | ||
| Elongation at Yield | 3.5 % | 3.5 % | ISO 527-1/-2 | ||
| Tensile Modulus | 4.70 GPa | 682 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | ||
| 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | ||
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | IEC 60093 | ||
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz |
3.6 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 3.7 @Frequency 100 Hz |
3.7 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0050 @Frequency 100 Hz |
0.0050 @Frequency 100 Hz |
IEC 60250 | ||
| 0.060 @Frequency 1.00e+6 Hz |
0.060 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 225 V | 225 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 50.0 °C | 122 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 205 °C | 401 °F | 50°C/h 50N; ISO 306 | ||
| Flammability, UL94 | V-0 @Thickness 0.400 mm |
V-0 @Thickness 0.0157 in |
IEC 60695-11-10 | ||
| Oxygen Index | 31 % | 31 % | ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 | ||
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 | ||
| De |
|||||
| Additives | Flame retarding agent | ||||
| Release agent | |||||
| Features | Flame retardant | ||||
| Form | Pellets | ||||
| ISO Shortname | ISO 7792-1-PBT,GFHMR,11-050,GF7; ISO 1043-PBT GF FR(17) | ||||
| Processing | Injection molding | ||||
| Region | Asia Pacific | ||||
| Europe | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
上海松翰塑化科技有限公司！本公司承諾，假一賠百！所有產(chǎn)品都是原廠家，原包裝一線獨(dú)家營銷！
我司所銷售所有產(chǎn)品均為原廠原包，均可提供相關(guān)資料報告（如：物性表，MSDS報告，UL報告，COA報告，SGS報告，F(xiàn)DA等）！
歡迎新老客戶來電或QQ咨詢：
聯(lián)系人：李先生
聯(lián)系電話；13636696005
聯(lián)系QQ；1020580970
聯(lián)系郵箱；1020580970@qq.com