| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | |||
| 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 | |||
| Water Absorption | 0.33 % @Thickness 2.00 mm |
0.33 % @Thickness 0.0787 in |
Sim. to ISO 62 | ||
| Moisture Absorption | 0.140 % @Thickness 2.00 mm |
0.140 % @Thickness 0.0787 in |
Sim. to ISO 62 | ||
| Viscosity | 102700 cP @Shear Rate 5000 1/s, Temperature 260 °C |
102700 cP @Shear Rate 5000 1/s, Temperature 500 °F |
ISO 11403-1 -2 | ||
| 122300 cP @Shear Rate 5000 1/s, Temperature 250 °C |
122300 cP @Shear Rate 5000 1/s, Temperature 482 °F |
ISO 11403-1 -2 | |||
| 147800 cP @Shear Rate 5000 1/s, Temperature 240 °C |
147800 cP @Shear Rate 5000 1/s, Temperature 464 °F |
ISO 11403-1 -2 | |||
| 310520 cP @Shear Rate 500 1/s, Temperature 260 °C |
310520 cP @Shear Rate 500 1/s, Temperature 500 °F |
ISO 11403-1 -2 | |||
| 375900 cP @Shear Rate 500 1/s, Temperature 250 °C |
375900 cP @Shear Rate 500 1/s, Temperature 482 °F |
ISO 11403-1 -2 | |||
| 460190 cP @Shear Rate 500 1/s, Temperature 240 °C |
460190 cP @Shear Rate 500 1/s, Temperature 464 °F |
ISO 11403-1 -2 | |||
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4 2577 | ||
| 0.0080 cm/cm | 0.0080 in/in | annealed; ISO 294-4 | |||
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | ISO 294-4 2577 | ||
| 0.015 cm/cm | 0.015 in/in | annealed; ISO 294-4 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-1/-2 | ||
| Elongation at Break | 3.4 % | 3.4 % | ISO 527-1/-2 | ||
| Tensile Modulus | 7.20 GPa | 1040 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 155 MPa | 22500 psi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO 180/1A | ||
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | ISO 180/1U | ||
| 32.0 kJ/m² @Temperature -30.0 °C |
15.2 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U | |||
| Charpy Impact Unnotched | 5.30 J/cm² | 25.2 ft-lb/in² | ISO 179/1eU | ||
| 4.40 J/cm² @Temperature -30.0 °C |
20.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1eA | ||
| 0.710 J/cm² @Temperature -30.0 °C |
3.38 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 6000 MPa @Time 3600 sec |
870000 psi @Time 1.00 hour |
ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 4800 MPa @Time 3.60e+6 sec |
696000 psi @Time 1000 hour |
ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 3.7 @Frequency 100 Hz |
3.7 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
IEC 60250 | ||
| 0.017 @Frequency 1.00e+6 Hz |
0.017 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C | 27.8 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 | ||
| Specific Heat Capacity | 1.74 J/g-°C | 0.416 BTU/lb-°F | |||
| Thermal Conductivity | 0.270 W/m-K | 1.87 BTU-in/hr-ft²-°F | of melt | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 207 °C | 405 °F | 50°C/h 50N; ISO 306 | ||
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
IEC 60695-11-10 | ||
| V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
IEC 60695-11-10 | |||
| Oxygen Index | 31 % | 31 % | ISO 4589-1/-2 | ||
| De |
|||||
| Delivery form | Pellets | ||||
| Part Marking Code | >PBT-GF15FR(17)< | ISO 11469 | |||
| Processing | Injection Moulding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PBT-GF15FR(17) | ||||
| UL recognition | UL | ||||
圖：
上海松翰塑化科技有限公司！本公司承諾，假一賠百！所有產(chǎn)品都是原廠家，原包裝一線獨家營銷！
我司所銷售所有產(chǎn)品均為原廠原包，均可提供相關(guān)資料報告（如：物性表，MSDS報告，UL報告，COA報告，SGS報告，F(xiàn)DA等）！
歡迎新老客戶來電或QQ咨詢：
聯(lián)系人：李先生
聯(lián)系電話；13636696005
聯(lián)系QQ；1020580970
聯(lián)系郵箱；1020580970@qq.com