物性表：

Physical Properties	Metric	English	Comments

Density	1.22 g/cc	0.0441 lb/in³
	1.42 g/cc	0.0513 lb/in³	ISO 1183
Water Absorption	0.40 % @Thickness 2.00 mm	0.40 % @Thickness 0.0787 in	Sim. to ISO 62
Moisture Absorption	0.150 % @Thickness 2.00 mm	0.150 % @Thickness 0.0787 in	Sim. to ISO 62
Viscosity	54480 cP @Shear Rate 5000 1/s, Temperature 260 °C	54480 cP @Shear Rate 5000 1/s, Temperature 500 °F	ISO 11403-1 -2
	65970 cP @Shear Rate 5000 1/s, Temperature 250 °C	65970 cP @Shear Rate 5000 1/s, Temperature 482 °F	ISO 11403-1 -2
	81200 cP @Shear Rate 5000 1/s, Temperature 240 °C	81200 cP @Shear Rate 5000 1/s, Temperature 464 °F	ISO 11403-1 -2
	152700 cP @Shear Rate 500 1/s, Temperature 260 °C	152700 cP @Shear Rate 500 1/s, Temperature 500 °F	ISO 11403-1 -2
	187800 cP @Shear Rate 500 1/s, Temperature 250 °C	187800 cP @Shear Rate 500 1/s, Temperature 482 °F	ISO 11403-1 -2
	234000 cP @Shear Rate 500 1/s, Temperature 240 °C	234000 cP @Shear Rate 500 1/s, Temperature 464 °F	ISO 11403-1 -2
Linear Mold Shrinkage, Flow	0.0040 cm/cm	0.0040 in/in	ISO 294-4 2577
Linear Mold Shrinkage, Transverse	0.011 cm/cm	0.011 in/in	ISO 294-4 2577

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	110 MPa	16000 psi	ISO 527-1/-2
Tensile Stress	9.443 MPa @Strain 0.546765 %, Temperature 160 °C	1370 psi @Strain 0.546765 %, Temperature 320 °F	ISO 11403-1 -2
	10.44 MPa @Strain 0.543915 %, Temperature 140 °C	1514 psi @Strain 0.543915 %, Temperature 284 °F	ISO 11403-1 -2
	13.88 MPa @Strain 0.298656 %, Temperature 40.0 °C	2013 psi @Strain 0.298656 %, Temperature 104 °F	ISO 11403-1 -2
	15.16 MPa @Strain 0.239814 %, Temperature -40.0 °C	2198 psi @Strain 0.239814 %, Temperature -40.0 °F	ISO 11403-1 -2
	15.89 MPa @Strain 0.268361 %, Temperature 23.0 °C	2304 psi @Strain 0.268361 %, Temperature 73.4 °F	ISO 11403-1 -2
	16.44 MPa @Strain 0.263749 %, Temperature -20.0 °C	2384 psi @Strain 0.263749 %, Temperature -4.00 °F	ISO 11403-1 -2
	19.57 MPa @Strain 1.3907 %, Temperature 160 °C	2839 psi @Strain 1.3907 %, Temperature 320 °F	ISO 11403-1 -2
	20.30 MPa @Strain 0.332444 %, Temperature 0.000 °C	2945 psi @Strain 0.332444 %, Temperature 32.0 °F	ISO 11403-1 -2
	20.39 MPa @Strain 1.23103 %, Temperature 140 °C	2957 psi @Strain 1.23103 %, Temperature 284 °F	ISO 11403-1 -2
	25.94 MPa @Strain 2.21207 %, Temperature 160 °C	3762 psi @Strain 2.21207 %, Temperature 320 °F	ISO 11403-1 -2
	28.35 MPa @Strain 2.01089 %, Temperature 140 °C	4111 psi @Strain 2.01089 %, Temperature 284 °F	ISO 11403-1 -2
	30.25 MPa @Strain 0.682024 %, Temperature 40.0 °C	4387 psi @Strain 0.682024 %, Temperature 104 °F	ISO 11403-1 -2
	30.59 MPa @Strain 3.09033 %, Temperature 160 °C	4437 psi @Strain 3.09033 %, Temperature 320 °F	ISO 11403-1 -2
	32.37 MPa @Strain 0.525841 %, Temperature -20.0 °C	4695 psi @Strain 0.525841 %, Temperature -4.00 °F	ISO 11403-1 -2
	32.91 MPa @Strain 0.527955 %, Temperature -40.0 °C	4774 psi @Strain 0.527955 %, Temperature -40.0 °F	ISO 11403-1 -2
	34.51 MPa @Strain 2.90782 %, Temperature 140 °C	5006 psi @Strain 2.90782 %, Temperature 284 °F	ISO 11403-1 -2
	34.73 MPa @Strain 0.597341 %, Temperature 23.0 °C	5037 psi @Strain 0.597341 %, Temperature 73.4 °F	ISO 11403-1 -2
	35.17 MPa @Strain 0.579891 %, Temperature 0.000 °C	5101 psi @Strain 0.579891 %, Temperature 32.0 °F	ISO 11403-1 -2
	46.94 MPa @Strain 1.13289 %, Temperature 40.0 °C	6808 psi @Strain 1.13289 %, Temperature 104 °F	ISO 11403-1 -2
	47.47 MPa @Strain 0.779352 %, Temperature -20.0 °C	6886 psi @Strain 0.779352 %, Temperature -4.00 °F	ISO 11403-1 -2
	49.06 MPa @Strain 0.795618 %, Temperature -40.0 °C	7116 psi @Strain 0.795618 %, Temperature -40.0 °F	ISO 11403-1 -2
	51.90 MPa @Strain 0.872047 %, Temperature 0.000 °C	7527 psi @Strain 0.872047 %, Temperature 32.0 °F	ISO 11403-1 -2
	54.34 MPa @Strain 0.971766 %, Temperature 23.0 °C	7881 psi @Strain 0.971766 %, Temperature 73.4 °F	ISO 11403-1 -2
	62.24 MPa @Strain 1.66228 %, Temperature 40.0 °C	9027 psi @Strain 1.66228 %, Temperature 104 °F	ISO 11403-1 -2
	63.03 MPa @Strain 1.05428 %, Temperature -20.0 °C	9142 psi @Strain 1.05428 %, Temperature -4.00 °F	ISO 11403-1 -2
	64.96 MPa @Strain 1.07013 %, Temperature -40.0 °C	9422 psi @Strain 1.07013 %, Temperature -40.0 °F	ISO 11403-1 -2
	69.141 MPa @Strain 1.20176 %, Temperature 0.000 °C	10028 psi @Strain 1.20176 %, Temperature 32.0 °F	ISO 11403-1 -2
	73.73 MPa @Strain 1.40132 %, Temperature 23.0 °C	10690 psi @Strain 1.40132 %, Temperature 73.4 °F	ISO 11403-1 -2
	107.5 MPa @Strain 2.00763 %, Temperature -20.0 °C	15590 psi @Strain 2.00763 %, Temperature -4.00 °F	ISO 11403-1 -2
	110.99 MPa @Strain 2.0059 %, Temperature -40.0 °C	16098 psi @Strain 2.0059 %, Temperature -40.0 °F	ISO 11403-1 -2
Elongation at Break	3.3 %	3.3 %	ISO 527-1/-2
Tensile Modulus	6.00 GPa	870 ksi	ISO 527-1/-2
Secant Modulus	1.23 GPa @Strain 4.12508 %, Temperature 100 °C	179 ksi @Strain 4.12508 %, Temperature 212 °F	ISO 11403-1 -2
	1.2757 GPa @Strain 4.5039 %, Temperature 80.0 °C	185.03 ksi @Strain 4.5039 %, Temperature 176 °F	ISO 11403-1 -2
	1.78 GPa @Strain 2.20401 %, Temperature 100 °C	258 ksi @Strain 2.20401 %, Temperature 212 °F	ISO 11403-1 -2
	2.06 GPa @Strain 2.00926 %, Temperature 80.0 °C	298 ksi @Strain 2.00926 %, Temperature 176 °F	ISO 11403-1 -2
	2.20 GPa @Strain 1.02372 %, Temperature 100 °C	319 ksi @Strain 1.02372 %, Temperature 212 °F	ISO 11403-1 -2
	2.3886 GPa @Strain 1.11375 %, Temperature 80.0 °C	346.44 ksi @Strain 1.11375 %, Temperature 176 °F	ISO 11403-1 -2
	2.45 GPa @Strain 0.411103 %, Temperature 100 °C	355 ksi @Strain 0.411103 %, Temperature 212 °F	ISO 11403-1 -2
	2.68 GPa @Strain 0.437002 %, Temperature 80.0 °C	388 ksi @Strain 0.437002 %, Temperature 176 °F	ISO 11403-1 -2
	2.7596 GPa @Strain 3.00056 %, Temperature 40.0 °C	400.25 ksi @Strain 3.00056 %, Temperature 104 °F	ISO 11403-1 -2
	3.43 GPa @Strain 2.06534 %, Temperature 40.0 °C	497 ksi @Strain 2.06534 %, Temperature 104 °F	ISO 11403-1 -2
	4.0227 GPa @Strain 1.30015 %, Temperature 40.0 °C	583.45 ksi @Strain 1.30015 %, Temperature 104 °F	ISO 11403-1 -2
	4.10 GPa @Strain 2.5045 %, Temperature 23.0 °C	595 ksi @Strain 2.5045 %, Temperature 73.4 °F	ISO 11403-1 -2
	4.44 GPa @Strain 0.682024 %, Temperature 40.0 °C	643 ksi @Strain 0.682024 %, Temperature 104 °F	ISO 11403-1 -2
	4.65 GPa @Strain 0.298656 %, Temperature 40.0 °C	674 ksi @Strain 0.298656 %, Temperature 104 °F	ISO 11403-1 -2
	4.97 GPa @Strain 1.72197 %, Temperature 23.0 °C	721 ksi @Strain 1.72197 %, Temperature 73.4 °F	ISO 11403-1 -2
	5.14 GPa @Strain 1.96921 %, Temperature 0.000 °C	745 ksi @Strain 1.96921 %, Temperature 32.0 °F	ISO 11403-1 -2
	5.49 GPa @Strain 1.11022 %, Temperature 23.0 °C	796 ksi @Strain 1.11022 %, Temperature 73.4 °F	ISO 11403-1 -2
	5.59 GPa @Strain 1.44095 %, Temperature 0.000 °C	810 ksi @Strain 1.44095 %, Temperature 32.0 °F	ISO 11403-1 -2
	5.61 GPa @Strain 1.66598 %, Temperature -20.0 °C	814 ksi @Strain 1.66598 %, Temperature -4.00 °F	ISO 11403-1 -2
	5.75 GPa @Strain 1.67592 %, Temperature -40.0 °C	833 ksi @Strain 1.67592 %, Temperature -40.0 °F	ISO 11403-1 -2
	5.81 GPa @Strain 0.597341 %, Temperature 23.0 °C	843 ksi @Strain 0.597341 %, Temperature 73.4 °F	ISO 11403-1 -2
	5.88 GPa @Strain 1.24902 %, Temperature -20.0 °C	852 ksi @Strain 1.24902 %, Temperature -4.00 °F	ISO 11403-1 -2
	5.89 GPa @Strain 0.97819 %, Temperature 0.000 °C	855 ksi @Strain 0.97819 %, Temperature 32.0 °F	ISO 11403-1 -2
	5.92 GPa @Strain 0.268361 %, Temperature 23.0 °C	859 ksi @Strain 0.268361 %, Temperature 73.4 °F	ISO 11403-1 -2
	5.98 GPa @Strain 1.26366 %, Temperature -40.0 °C	867 ksi @Strain 1.26366 %, Temperature -40.0 °F	ISO 11403-1 -2
	6.06 GPa @Strain 0.869061 %, Temperature -20.0 °C	879 ksi @Strain 0.869061 %, Temperature -4.00 °F	ISO 11403-1 -2
	6.07 GPa @Strain 0.579891 %, Temperature 0.000 °C	880 ksi @Strain 0.579891 %, Temperature 32.0 °F	ISO 11403-1 -2
	6.11 GPa @Strain 0.332444 %, Temperature 0.000 °C	886 ksi @Strain 0.332444 %, Temperature 32.0 °F	ISO 11403-1 -2
	6.14 GPa @Strain 0.884826 %, Temperature -40.0 °C	891 ksi @Strain 0.884826 %, Temperature -40.0 °F	ISO 11403-1 -2
	6.16 GPa @Strain 0.525841 %, Temperature -20.0 °C	893 ksi @Strain 0.525841 %, Temperature -4.00 °F	ISO 11403-1 -2
	6.23 GPa @Strain 0.263749 %, Temperature -20.0 °C	904 ksi @Strain 0.263749 %, Temperature -4.00 °F	ISO 11403-1 -2
	6.23 GPa @Strain 0.527955 %, Temperature -40.0 °C	904 ksi @Strain 0.527955 %, Temperature -40.0 °F	ISO 11403-1 -2
	6.32 GPa @Strain 0.239814 %, Temperature -40.0 °C	917 ksi @Strain 0.239814 %, Temperature -40.0 °F	ISO 11403-1 -2
Charpy Impact Unnotched	3.00 J/cm²	14.3 ft-lb/in²	ISO 179/1eU
	3.00 J/cm² @Temperature -30.0 °C	14.3 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
Charpy Impact, Notched	0.550 J/cm²	2.62 ft-lb/in²	ISO 179/1eA

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm	IEC 60093
Surface Resistance	1.00e+15 ohm	1.00e+15 ohm	IEC 60093
Dielectric Constant	3.5 @Frequency 1.00e+6 Hz	3.5 @Frequency 1.00e+6 Hz	IEC 60250
	4.1 @Frequency 100 Hz	4.1 @Frequency 100 Hz	IEC 60250
Dielectric Strength	27.0 kV/mm	686 kV/in	IEC 60243-1
Dissipation Factor	0.0020 @Frequency 100 Hz	0.0020 @Frequency 100 Hz	IEC 60250
	0.020 @Frequency 1.00e+6 Hz	0.020 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	350 V	350 V	IEC 60112

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	50.0 µm/m-°C	27.8 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	95.0 µm/m-°C	52.8 µin/in-°F	ISO 11359-1/-2
Specific Heat Capacity	1.90 J/g-°C	0.454 BTU/lb-°F
Thermal Conductivity	0.240 W/m-K	1.67 BTU-in/hr-ft²-°F	of melt
Melting Point	224 °C	435 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	200 °C	392 °F	ISO 75-1/-2
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	IEC 60695-11-10
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in	IEC 60695-11-10
Oxygen Index	19 %	19 %	ISO 4589-1/-2

Descriptive Properties
Additives	Release agent
Delivery form	Pellets
Part Marking Code	>PBT-GF15<	ISO 11469
Processing	Injection Moulding
Regional Availability	Asia Pacific
	Europe
	Global
	Near East/Africa
	North America
	South and Central America
Resin Identification	PBT-GF15
UL recognition	UL

圖：

上海松翰塑化科技有限公司！本公司承諾，假一賠百！所有產品都是原廠家，原包裝一線獨家營銷！

我司所銷售所有產品均為原廠原包，均可提供相關資料報告（如：物性表，MSDS報告，UL報告，COA報告，SGS報告，FDA等）！

歡迎新老客戶來電或QQ咨詢：

聯系人：李先生

聯系電話；13636696005

聯系QQ；1020580970

聯系郵箱；1020580970@qq.com

杜邦高性能聚合物sk612sf NC010/20%的玻纖填充