| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | |||
| 1.66 g/cc | 0.0600 lb/in³ | ISO 1183 | |||
| Water Absorption | 0.30 % @Thickness 2.00 mm |
0.30 % @Thickness 0.0787 in |
Sim. to ISO 62 | ||
| Moisture Absorption | 0.100 % @Thickness 2.00 mm |
0.100 % @Thickness 0.0787 in |
Sim. to ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | ISO 294-4 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 140 MPa | 20300 psi | ISO 527-1/-2 | ||
| Tensile Stress | 18.7 MPa @Strain 0.270 %, Temperature 90.0 °C |
2710 psi @Strain 0.270 %, Temperature 194 °F |
ISO 11403-1 -2 | ||
| 20.51 MPa @Strain 0.150 %, Temperature 23.0 °C |
2975 psi @Strain 0.150 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 21.01 MPa @Strain 0.210 %, Temperature 40.0 °C |
3047 psi @Strain 0.210 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 43.69 MPa @Strain 0.800 %, Temperature 90.0 °C |
6337 psi @Strain 0.800 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
| 59.23 MPa @Strain 1.42 %, Temperature 90.0 °C |
8591 psi @Strain 1.42 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
| 65.6 MPa @Strain 0.750 %, Temperature 40.0 °C |
9510 psi @Strain 0.750 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 67.39 MPa @Strain 2.03 %, Temperature 90.0 °C |
9774 psi @Strain 2.03 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
| 71.91 MPa @Strain 0.580 %, Temperature 23.0 °C |
10430 psi @Strain 0.580 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 91.43 MPa @Strain 1.30 %, Temperature 40.0 °C |
13260 psi @Strain 1.30 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 108.1 MPa @Strain 1.00 %, Temperature 23.0 °C |
15680 psi @Strain 1.00 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 129.8 MPa @Strain 1.43 %, Temperature 23.0 °C |
18830 psi @Strain 1.43 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 14.2 GPa | 2060 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 | ||
| Flexural Modulus | 13.3 GPa | 1930 ksi | ISO 178 | ||
| Shear Modulus | 0.6417 GPa @Temperature 160 °C |
93.07 ksi @Temperature 320 °F |
Dynamic; ISO 11403-1 -2 | ||
| 0.812 GPa @Temperature 120 °C |
118 ksi @Temperature 248 °F |
Dynamic; ISO 11403-1 -2 | |||
| 1.167 GPa @Temperature 70.0 °C |
169.2 ksi @Temperature 158 °F |
Dynamic; ISO 11403-1 -2 | |||
| 2.263 GPa @Temperature 20.0 °C |
328.3 ksi @Temperature 68.0 °F |
Dynamic; ISO 11403-1 -2 | |||
| 2.438 GPa @Temperature -20.0 °C |
353.7 ksi @Temperature -4.00 °F |
Dynamic; ISO 11403-1 -2 | |||
| 2.578 GPa @Temperature -50.0 °C |
374.0 ksi @Temperature -58.0 °F |
Dynamic; ISO 11403-1 -2 | |||
| Secant Modulus | 6.275 GPa @Strain 1.60 %, Temperature 40.0 °C |
910.1 ksi @Strain 1.60 %, Temperature 104 °F |
ISO 11403-1 -2 | ||
| 8.75 GPa @Strain 0.750 %, Temperature 40.0 °C |
1270 ksi @Strain 0.750 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 10.0 GPa @Strain 0.210 %, Temperature 40.0 °C |
1450 ksi @Strain 0.210 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 10.193 GPa @Strain 1.14 %, Temperature 23.0 °C |
1478.4 ksi @Strain 1.14 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 12.4 GPa @Strain 0.580 %, Temperature 23.0 °C |
1800 ksi @Strain 0.580 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 13.7 GPa @Strain 0.150 %, Temperature 23.0 °C |
1980 ksi @Strain 0.150 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO 180/1A | ||
| 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A | |||
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | ISO 179/1eU | ||
| 6.50 J/cm² @Temperature -30.0 °C |
30.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.9 @Frequency 1.00e+6 Hz |
3.9 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 4.1 @Frequency 100 Hz |
4.1 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0038 @Frequency 100 Hz |
0.0038 @Frequency 100 Hz |
IEC 60250 | ||
| 0.013 @Frequency 1.00e+6 Hz |
0.013 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 475 V | 475 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 222 °C | 432 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 215 °C | 419 °F | 50°C/h 50N; ISO 306 | ||
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 | ||
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
IEC 60695-11-10 | |||
| Oxygen Index | 20 % | 20 % | ISO 4589-1/-2 | ||
| De |
|||||
| Additives | Release agent | ||||
| Delivery form | Pellets | ||||
| Part Marking Code | >PBT-GF45< | ISO 11469 | |||
| Processing | Injection Moulding | ||||
| Other Extrusion | |||||
| Profile Extrusion | |||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PBT-GF45 | ||||
| UL recognition | UL | ||||
圖：
上海松翰塑化科技有限公司！本公司承諾，假一賠百！所有產品都是原廠家，原包裝一線獨家營銷！
我司所銷售所有產品均為原廠原包，均可提供相關資料報告（如：物性表，MSDS報告，UL報告，COA報告，SGS報告，FDA等）！
歡迎新老客戶來電或QQ咨詢：
聯系人：李先生
聯系電話；13636696005
聯系QQ；1020580970
聯系郵箱；1020580970@qq.com