LCP C130HS 材料說明：液晶聚合物樹脂：sepaz LCP樹脂具有傳統塑料的一種獨特的結構和性能沒有想到的。在sepaz LCP以優異的綜合性能和成型效率。sepaz LCP具有獨特的屬性，產品變得更薄，更大的機械強度。sepaz LCP連接器發現使用，傳感器和其他電子元件和CD提取部分，在復印機和傳真辦公和視聽設備部件。
LCP C130HS 加工方法：注塑成型
LCP c130hs 性質參數表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.66 g/cc | 1.66 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0012 cm/cm | 0.0012 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 151.1 MPa | 21910 psi | ASTM D638 |
| Elongation at Break | 2.1 % | 2.1 % | ASTM D638 |
| Flexural Strength | 196.2 MPa | 28460 psi | ASTM D790 |
| Flexural Modulus | 14.52 GPa | 2106 ksi | ASTM D790 |
| Izod Impact, Notched | 0.981 J/cm | 1.84 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 335 °C | 635 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 350 - 370 °C | 662 - 698 °F | |
| Mold Temperature | 30.0 - 95.0 °C | 86.0 - 203 °F | |