LCP 6130lx 材料說明：澤尼特«6130lx是注塑成型的30%玻璃纖維增強液晶聚合物。它非常適合各種苛刻的應用。
LCP 6130lx 加工方法：注塑成型
LCP 6130lx 性能參數表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00120 cm/cm | 0.00120 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00600 cm/cm | 0.00600 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 145 MPa | 21000 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 2.00 % | 2.00 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 15.0 GPa | 2180 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
| Flexural Modulus | 12.8 GPa | 1860 ksi | ISO 178 |
| Compressive Strength | 133 MPa | 19300 psi | ISO 604 |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179/1eA |
| 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 4.00 @Frequency 1.00e+6 Hz |
4.00 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.27 @Frequency 2.05e+9 Hz |
4.27 @Frequency 2.05e+9 Hz |
||
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0310 @Frequency 1.00e+6 Hz |
0.0310 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 60.0 @Frequency 2.05e+9 Hz |
60.0 @Frequency 2.05e+9 Hz |
||
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |