| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 3.70 % | 3.70 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | Sim. To ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm | 0.020 in/in | Sm. To ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | cond; ISO 527-1/-2 |
| 100 MPa | 14500 psi | dry; ISO 527-1/-2 | |
| 30.0 MPa @Temperature 200 °C |
4350 psi @Temperature 392 °F |
ISO 527-1/-2 | |
| 35.0 MPa @Temperature 180 °C |
5080 psi @Temperature 356 °F |
ISO 527-1/-2 | |
| 40.0 MPa @Temperature 160 °C |
5800 psi @Temperature 320 °F |
ISO 527-1/-2 | |
| 50.0 MPa @Temperature 120 °C |
7250 psi @Temperature 248 °F |
ISO 527-1/-2 | |
| Elongation at Break | 40 % | 40 % | dry; ISO 527-1/-2 |
| >= 50 % | >= 50 % | cond; ISO 527-1/-2 | |
| >= 50 % @Temperature 120 °C |
>= 50 % @Temperature 248 °F |
ISO 527-1/-2 | |
| >= 50 % @Temperature 160 °C |
>= 50 % @Temperature 320 °F |
ISO 527-1/-2 | |
| >= 50 % @Temperature 180 °C |
>= 50 % @Temperature 356 °F |
ISO 527-1/-2 | |
| >= 50 % @Temperature 200 °C |
>= 50 % @Temperature 392 °F |
ISO 527-1/-2 | |
| Tensile Modulus | 1.00 GPa | 145 ksi | cond; ISO 527-1/-2 |
| 3.30 GPa | 479 ksi | dry; ISO 527-1/-2 | |
| 0.500 GPa @Temperature 200 °C |
72.5 ksi @Temperature 392 °F |
ISO 527-1/-2 | |
| 0.600 GPa @Temperature 180 °C |
87.0 ksi @Temperature 356 °F |
ISO 527-1/-2 | |
| 0.650 GPa @Temperature 160 °C |
94.3 ksi @Temperature 320 °F |
ISO 527-1/-2 | |
| 0.800 GPa @Temperature 120 °C |
116 ksi @Temperature 248 °F |
ISO 527-1/-2 | |
| Flexural Modulus | 0.900 GPa | 131 ksi | cond; ISO 178 |
| 3.00 GPa | 435 ksi | dry; ISO 178 | |
| 0.600 GPa @Temperature 160 °C |
87.0 ksi @Temperature 320 °F |
ISO 178 | |
| 0.800 GPa @Temperature 120 °C |
116 ksi @Temperature 248 °F |
ISO 178 | |
| Fatigue Strength | 12.0 MPa @# of Cycles 1.00e+8 , Temperature 140 °C |
1740 psi @# of Cycles 1.00e+8 , Temperature 284 °F |
R = 0.1, 8 Hz, dry |
| 21.0 MPa @# of Cycles 1.00e+7 , Temperature 140 °C |
3050 psi @# of Cycles 1.00e+7 , Temperature 284 °F |
R = 0.1, 8 Hz, dry | |
| 30.0 MPa @# of Cycles 1.00e+6 , Temperature 140 °C |
4350 psi @# of Cycles 1.00e+6 , Temperature 284 °F |
R = 0.1, 8 Hz, dry | |
| 35.0 MPa @# of Cycles 100000 , Temperature 140 °C |
5080 psi @# of Cycles 100000 , Temperature 284 °F |
R = 0.1, 8 Hz, dry | |
| 37.0 MPa @# of Cycles 10000 , Temperature 140 °C |
5370 psi @# of Cycles 10000 , Temperature 284 °F |
R = 0.1, 8 Hz, dry | |
| 39.0 MPa @# of Cycles 1000 , Temperature 140 °C |
5660 psi @# of Cycles 1000 , Temperature 284 °F |
R = 0.1, 8 Hz, dry | |
| 41.0 MPa @# of Cycles 100 , Temperature 140 °C |
5950 psi @# of Cycles 100 , Temperature 284 °F |
R = 0.1, 8 Hz, dry | |
| Izod Impact Resistance | 0.400 J/cm² @Temperature -40.0 °C |
1.90 ft-lb/in² @Temperature -40.0 °F |
cond; ISO 180/1A |
| 0.400 J/cm² @Temperature -40.0 °C |
1.90 ft-lb/in² @Temperature -40.0 °F |
dry; ISO 180/1A | |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 180/1A | |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 180/1A | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
cond; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
cond; ISO 179/1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
dry; ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eA |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA | |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | cond; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | dry; IEC 60093 | |
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | cond; IEC 60243-1 |
| 25.0 kV/mm | 635 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 400 V | 400 V | dry; IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 85.0 µm/m-°C | 47.2 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 152 °C | 306 °F | 5000 hours Thermal Index; IEC 60216/ISO 527-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | dry; ISO 75-1/-2 |
概述
PA塑料(尼龍，聚酰胺)，英文名稱:Polyamide
PA的品種繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近幾年開發(fā)的半芳香族尼龍PA6T和特種尼龍等很多新品種。
物理性能
比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米
成型收縮率：PA6 0.8-2.5% ，PA66 1.5-2.2%
成型溫度：220-300℃
干燥條件：100-110℃/12小時
堅韌、耐磨、耐油、,耐水、抗酶菌、但吸水大
燃燒鑒別方法：火焰上端黃色，下端藍(lán)色，燃燒后塑料熔滴落，起泡，離火后特殊的羊毛，指甲燒焦味和帶芹菜味
|
尼龍6： |
彈性好，沖擊強度，吸水較大 |
|
尼龍66： |
性能優(yōu)于尼龍6，強度高，耐磨性好 |
|
尼龍610： |
與尼龍66相似，但吸水小，剛度低 |
|
尼龍1010： |
半透明，吸水小。耐寒性較好。適于制作一般機械零件、減磨耐磨零件、傳動零件以及化工、電器、儀表等零件 |
成型性能
1、結(jié)晶料，熔點較高，熔融溫度范圍窄，熱穩(wěn)定性差，料溫超過300度、滯留時間超過30分鐘即分解。較易吸濕，需干燥，含水量不得超過0.3%。
2、流動性好，易溢料。宜用自鎖時噴嘴，并應(yīng)加熱。
3、成型收縮范圍及收縮率大，方向性明顯，易發(fā)生縮孔、變形等。
4、模溫按塑件壁厚在20～90度范圍內(nèi)選取，注射壓力按注射機類型、料溫、塑件形狀尺寸、模具澆注系統(tǒng)選定，成型周期按塑件壁厚選定。樹脂粘度小時，注射、冷卻時間應(yīng)取長，并用白油作脫模劑。
5、模具澆注系統(tǒng)的形式和尺寸，增大流道和澆口尺寸可減少縮水。
聚酰胺的不足之處在于：由于熱膨脹和吸水性所至的尺寸精度不夠，耐酸性差，硬度和彈性模量不夠。經(jīng)改良以后，也是比較優(yōu)秀的工程塑料之一。
應(yīng)用
汽車制造方面
用于制造燃料濾網(wǎng)、燃料過濾器、罐、捕集器、儲油槽、發(fā)動機汽缸蓋罩、散熱器水缸、平衡旋轉(zhuǎn)軸齒輪。也可用在汽車的電器配件、接線柱等。另外，它還可用作驅(qū)動、控制部件等。
電器電子工業(yè)
可用于制造電飯鍋、電動吸塵器、高頻電子食品加熱器，電器產(chǎn)品的接線柱、開關(guān)和電阻器等。
醫(yī)療器械儀器
用于醫(yī)用輸血管、取血器、輸液器等。PA單絲可做外科手術(shù)縫線、假發(fā)等；另外，電子打字機的數(shù)字旋轉(zhuǎn)盤、接線柱、傳動齒輪、印刷機的帶式過濾片等。
其它方面
用于制作一次性打火機體、堿性干電池襯墊，摩托車駕駛員的頭盔，辦公機器外殼，辦公用椅的角輪、座和靠背，冰鞋、釣魚線等，PA薄膜氣體阻隔性能優(yōu)良，而且耐油性、耐低溫沖擊性、耐穿透性好，可用于肉、火腿腸等冷凍食品的包裝。聚酰胺還可棒材和板材，也作齒輪或其它傳動裝置。
上海浩銘塑膠有限公司！本公司承諾，所有產(chǎn)品都是原廠家，原包裝一線獨家營銷！
可提供以下報告：COA（產(chǎn)地證明）SGS（檢測報告）MSDS（成分報告）FDA（食品安全報告）UL黃卡（出口報告）正規(guī)發(fā)票！歡迎新老客戶來電咨詢：
聯(lián)系人：鄧小姐
聯(lián)系電話：13917657923
聯(lián)系QQ:996152797
聯(lián)系郵箱：996152797@qq.com