| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | |||
| Linear Mold Shrinkage, Flow | 0.023 - 0.027 cm/cm | 0.023 - 0.027 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.0235 - 0.0275 cm/cm | 0.0235 - 0.0275 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 35.0 MPa | 5080 psi | |||
| Elongation at Break | >= 100 % @Temperature 60.0 °C |
>= 100 % @Temperature 140 °F |
|||
| >= 100 % @Temperature 90.0 °C |
>= 100 % @Temperature 194 °F |
||||
| 100 % @Temperature 23.0 °C |
100 % @Temperature 73.4 °F |
||||
| Tensile Modulus | 0.500 GPa @Temperature 90.0 °C |
72.5 ksi @Temperature 194 °F |
|||
| 0.900 GPa @Temperature 60.0 °C |
131 ksi @Temperature 140 °F |
||||
| 1.50 GPa @Temperature 23.0 °C |
218 ksi @Temperature 73.4 °F |
||||
| Charpy Impact Unnotched | NB | NB | |||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 65.0 °C | 149 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | |||
| Vicat Softening Point | 125 °C @Load 5.00 kg |
257 °F @Load 11.0 lb |
|||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 175 - 200 °C | 347 - 392 °F | |||
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |||
| Drying Temperature | 80.0 - 90.0 °C @Time 10800 sec |
176 - 194 °F @Time 3.00 hour |
|||
| De |
|||||
| ISO Shrinkage - Pressure | 60 MPa | ||||
上海松翰塑化科技有限公司！本公司承諾，假一賠百！所有產品都是原廠家，原包裝一線獨家營銷！
我司所銷售所有產品均為原廠原包，均可提供相關資料報告（如：物性表，MSDS報告，UL報告，COA報告，SGS報告，FDA等）！
主要銷售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料產品的相關性能或是需要原料產品的相關報告，請您通過電話或是QQ與我聯系！
歡迎新老客戶來電或QQ咨詢：
聯系人：李先生
聯系電話；13636696005
聯系QQ；1020580970
聯系郵箱；1020580970@qq.com