| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | |||
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0055 cm/cm | 0.0030 - 0.0055 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.010 - 0.013 cm/cm | 0.010 - 0.013 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 65.0 MPa @Temperature 90.0 °C |
9430 psi @Temperature 194 °F |
|||
| 100 MPa @Temperature 60.0 °C |
14500 psi @Temperature 140 °F |
||||
| 120 MPa @Temperature 23.0 °C |
17400 psi @Temperature 73.4 °F |
||||
| Elongation at Break | 0.90 % @Temperature 23.0 °C |
0.90 % @Temperature 73.4 °F |
|||
| 1.1 % @Temperature 60.0 °C |
1.1 % @Temperature 140 °F |
||||
| 1.2 % @Temperature 90.0 °C |
1.2 % @Temperature 194 °F |
||||
| Tensile Modulus | 10.0 GPa @Temperature 90.0 °C |
1450 ksi @Temperature 194 °F |
|||
| 14.5 GPa @Temperature 60.0 °C |
2100 ksi @Temperature 140 °F |
||||
| 18.5 GPa @Temperature 23.0 °C |
2680 ksi @Temperature 73.4 °F |
||||
| Charpy Impact Unnotched | 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
|||
| 1.50 J/cm² @Temperature -20.0 °C |
7.14 ft-lb/in² @Temperature -4.00 °F |
||||
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -20.0 °C |
0.952 ft-lb/in² @Temperature -4.00 °F |
|||
| 0.250 J/cm² @Temperature 23.0 °C |
1.19 ft-lb/in² @Temperature 73.4 °F |
||||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 85.0 °C | 185 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | |||
| Vicat Softening Point | 165 °C @Load 5.00 kg |
329 °F @Load 11.0 lb |
|||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 180 - 210 °C | 356 - 410 °F | |||
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
| Drying Temperature | 80.0 - 90.0 °C @Time 10800 sec |
176 - 194 °F @Time 3.00 hour |
|||
| De |
|||||
| ISO Shrinkage - Pressure | 60 MPa | ||||
上海松翰塑化科技有限公司！本公司承諾，假一賠百！所有產品都是原廠家，原包裝一線獨家營銷！
我司所銷售所有產品均為原廠原包，均可提供相關資料報告（如：物性表，MSDS報告，UL報告，COA報告，SGS報告，FDA等）！
主要銷售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料產品的相關性能或是需要原料產品的相關報告，請您通過電話或是QQ與我聯系！
歡迎新老客戶來電或QQ咨詢：
聯系人：李先生
聯系電話；13636696005
聯系QQ；1020580970
聯系郵箱；1020580970@qq.com