| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | ISO 294-4 2577 | ||
| Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO 527-1/-2 | ||
| Elongation at Break | >= 50 % | >= 50 % | Nominal; ISO 527-1/-2 | ||
| Elongation at Yield | 30 % | 30 % | ISO 527-1/-2 | ||
| Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527-1/-2 | ||
| Flexural Modulus | 1.10 GPa | 160 ksi | ISO 178 | ||
| Shear Modulus | 0.0351 GPa @Temperature 160 °C |
5.09 ksi @Temperature 320 °F |
Dynamic; ISO 11403-1 -2 | ||
| 0.0816 GPa @Temperature 120 °C |
11.8 ksi @Temperature 248 °F |
Dynamic; ISO 11403-1 -2 | |||
| 0.1884 GPa @Temperature 70.0 °C |
27.33 ksi @Temperature 158 °F |
Dynamic; ISO 11403-1 -2 | |||
| 0.3691 GPa @Temperature 20.0 °C |
53.53 ksi @Temperature 68.0 °F |
Dynamic; ISO 11403-1 -2 | |||
| 0.5982 GPa @Temperature -20.0 °C |
86.76 ksi @Temperature -4.00 °F |
Dynamic; ISO 11403-1 -2 | |||
| 1.1904 GPa @Temperature -50.0 °C |
172.66 ksi @Temperature -58.0 °F |
Dynamic; ISO 11403-1 -2 | |||
| Charpy Impact, Notched | 8.00 J/cm² | 38.1 ft-lb/in² | ISO 179/1eA | ||
| 1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 | ||
| De |
|||||
| Additives | Lubricants | ||||
| Release agent | |||||
| Delivery form | Pellets | ||||
| Emissions | <8 mg/kg | VDA 275 | |||
| Part Marking Code | >POM-HI< | ISO 11469 | |||
| Processing | Blow Moulding | ||||
| Coatable | |||||
| Injection Moulding | |||||
| Other Extrusion | |||||
| Profile Extrusion | |||||
| Sheet Extrusion | |||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | POM-HI | ISO 1043 | |||
| UL recognition | UL | ||||
POM 的簡介
POM強(qiáng)度、剛度高，彈性好，減磨耐磨性好。其力學(xué)性能優(yōu)異，比強(qiáng)度可達(dá)50.5MPa，比剛度可達(dá)2650MPa，與金屬十分接近。POM的力學(xué)性能隨溫度變化小，共聚POM比均聚POM的變化稍大一點(diǎn)。
POM的沖擊強(qiáng)度較高，但常規(guī)沖擊不及ABS和PC；POM對(duì)缺口敏感，有缺口可使沖擊強(qiáng)度下降90%之多。
POM的疲勞強(qiáng)度十分突出，10交變載荷作用后，疲勞強(qiáng)度可達(dá)35MPa，而PA和PC僅為28MPa。
POM的蠕變性與PA相似，在20℃、21MPa、3000h時(shí)僅為2.3%，而且受溫度的影響很小。
POM的摩擦因數(shù)小，耐磨性好（POM>PA66>PA6>ABS>HPVC>PS>PC），極限PV值很大，自潤滑性好。
POM制品對(duì)磨時(shí)，高載荷作用時(shí)易產(chǎn)生類似尖叫的噪聲。
POM 化學(xué)性質(zhì)
POM 按分子鏈結(jié)構(gòu)不同，聚甲醛可分為均聚甲醛和共聚甲醛，前者密度、結(jié)晶度、熔點(diǎn)都高，但是熱穩(wěn)定性差，加工溫度窄（10度），對(duì)酸堿的穩(wěn)定性略低；后者密度、結(jié)晶度、熔點(diǎn)較低，但熱穩(wěn)定性好，不易分解，加工溫度寬（50度） 。
POM 不足之處在于：由受強(qiáng)酸腐蝕，耐侯差，粘合性差，熱分解與軟化溫度接近，限氧指數(shù)小。它們廣泛用于汽車工業(yè)，電子電器，機(jī)械設(shè)備等。還可以做水龍頭、框窗、洗漱盆。
POM具有很低的摩擦系數(shù)和很好的幾何穩(wěn)定性，特別適合于制作齒輪和軸承。由于它還具有耐高溫特性，因此還用于管道器件（管道閥門、泵殼體），草坪設(shè)備等。
POM 環(huán)境性能:
POM不耐強(qiáng)酸和氧化劑，對(duì)烯酸及弱酸有一定的穩(wěn)定性。
POM的耐溶劑性良好，可耐烴類、醇類、醛類、醚類、汽油、潤滑油及弱堿等，并可在高溫下保持相當(dāng)?shù)幕瘜W(xué)穩(wěn)定性。吸水性小，尺寸穩(wěn)定性好。
POM的耐候性不好，長期在紫外線作用下，力學(xué)性能下降，表面發(fā)生粉化和龜裂。
應(yīng)用范圍
POM屬結(jié)晶性塑料，熔點(diǎn)明顯，一旦達(dá)到熔點(diǎn)，熔體粘度迅速下降。當(dāng)溫度超過一定限度或熔體受熱時(shí)間過長，會(huì)引起分解。
POM具有較好的綜合性能，在熱塑性塑料中是最堅(jiān)硬的，是塑料材料中力學(xué)性能最接近金屬的品種之一，其抗張強(qiáng)度、彎曲強(qiáng)度、耐疲勞強(qiáng)度，耐磨性和電性都十分優(yōu)良，可在-40度--100度之間長期使用。
上海松翰塑化科技有限公司，供應(yīng)原料，品質(zhì)真實(shí),物實(shí)價(jià)廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
歡迎各位客戶前來咨詢：
聯(lián)系人： 夏先生
手 機(jī)：13501802636
QQ ：205730283
郵 箱 ：205730283@qq.com
參考圖如下：