、用途：
廣泛應用于機械、儀器儀表、汽車部件、電子電氣、鐵路、家電、通訊、紡機、體育休閑用品、油管、油箱及一些精密工程制品。
電子電器：連接器、卷線軸、計時器、護蓋斷路器、開關殼座。
汽車： 散熱風扇、門把、油箱蓋、進氣隔柵、水箱護蓋、燈座。
工業零件：椅座、自行車輸框、溜冰鞋底座、紡織梭、踏板、滑輸。
上海松翰塑化科技有限公司，供應原料，品質真實,物實價廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
歡迎各位客戶前來咨詢：
聯系人： 夏先生
手 機：13501802636
QQ ：205730283
郵 箱 ：205730283@qq.com
物性表:
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | Melt; ISO 1183 | ||
| 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 | |||
| Water Absorption | 0.90 % | 0.90 % | 24 hour; ISO Test | ||
| 5.5 % | 5.5 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ASTM Test | ||
| Tensile Strength at Break | 152 MPa | 22000 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 145 MPa | 21000 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.5 % | 3.5 % | 0.2 in/min; ASTM Test | ||
| 3.5 % | 3.5 % | 5mm/min; ISO 527 | |||
| Tensile Modulus | 9.30 GPa | 1350 ksi | 1mm/min; ISO 527 | ||
| 2.66 GPa @Temperature 120 °C |
386 ksi @Temperature 248 °F |
ISO Data | |||
| 9.20 GPa @Temperature -40.0 °C |
1330 ksi @Temperature -40.0 °F |
ISO Data | |||
| Flexural Strength | 215 MPa | 31200 psi | ISO Data | ||
| 241 MPa | 35000 psi | ASTM Test | |||
| 89.0 MPa @Temperature 120 °C |
12900 psi @Temperature 248 °F |
ASTM Test | |||
| 105 MPa @Temperature 93.0 °C |
15200 psi @Temperature 199 °F |
ASTM Test | |||
| 130 MPa @Temperature 65.0 °C |
18900 psi @Temperature 149 °F |
ASTM Test | |||
| 310 MPa @Temperature -40.0 °C |
45000 psi @Temperature -40.0 °F |
ASTM Test | |||
| Flexural Modulus | 7.20 GPa | 1040 ksi | ISO Data | ||
| 8.00 GPa | 1160 ksi | ASTM Test | |||
| 3.04 GPa @Temperature 120 °C |
441 ksi @Temperature 248 °F |
ASTM Test | |||
| 3.28 GPa @Temperature 93.0 °C |
476 ksi @Temperature 199 °F |
ASTM Test | |||
| 4.04 GPa @Temperature 65.0 °C |
586 ksi @Temperature 149 °F |
ASTM Test | |||
| Izod Impact, Notched | 2.39 J/cm @Thickness 3.17 mm |
4.48 ft-lb/in @Thickness 0.125 in |
ASTM Test | ||
| Izod Impact, Notched (ISO) | 21.0 kJ/m² | 9.99 ft-lb/in² | ISO Test | ||
| 14.0 kJ/m² @Temperature -40.0 °C |
6.66 ft-lb/in² @Temperature -40.0 °F |
ISO Test | |||
| Charpy Impact Unnotched | 7.80 J/cm² | 37.1 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179 | ||
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz |
3.4 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 3.6 @Frequency 100 Hz |
3.6 @Frequency 100 Hz |
IEC 60250 | |||
| 3.8 @Frequency 1e+9 Hz |
3.8 @Frequency 1e+9 Hz |
ASTM Data | |||
| 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
ASTM Data | |||
| Dielectric Strength | 43.0 kV/mm | 1090 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 0.010 @Frequency 100 Hz |
0.010 @Frequency 100 Hz |
IEC 60250 | |||
| 0.010 @Frequency 1e+9 Hz |
0.010 @Frequency 1e+9 Hz |
ASTM Data | |||
| 0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
ASTM Data | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 24.0 µm/m-°C | 13.3 µin/in-°F | ISO 11359 | ||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C | 46.7 µin/in-°F | ISO 11359 | ||
| Specific Heat Capacity | 1.958 J/g-°C | 0.4680 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | Melt | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75 | ||
| 210 °C | 410 °F | ASTM Test | |||
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
|||
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 95.0 °C | 203 °F | Injection molding | ||
| De |
|||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| UL.UL-C | Yes | ||||