PA6 8260HS BK-102 40%礦物、

  PA6 8260HS 塑膠原料為半透明或不透明乳白包或帶黃色顆粒狀結晶形聚合物，具有可塑性。密度（g/cm3） 1．10-1．14；拉伸強度(MPa) 60. 0-80．0；洛氏硬度118；熔點252℃；脆化溫度-30℃；熱分解溫度大于350℃；連續耐熱80-120℃；沖擊強度（kJ/m2） 60-100；靜彎曲強度(MPa) 1 00-120；馬丁耐熱(℃) 50-60；彎曲彈性模量 (MPa) 2000～3000；體積電阻率（Ωcm） 1.83×1015；平衡吸水率2．5%；介電常數 1．63。

Physical Properties	Metric	English	Comments
Density	1.49 g/cc	0.0538 lb/in³	ISO 1183
Water Absorption	1.1 %	1.1 %	24 hour; ISO Test
	5.7 %	5.7 %	ISO 62
Moisture Absorption at Equilibrium	1.6 %	1.6 %	23°C/50% R.H.; ISO 62
Linear Mold Shrinkage	0.0090 cm/cm	0.0090 in/in	ASTM Data; MD
Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	119	119	ASTM Test
Tensile Strength at Break	85.0 MPa	12300 psi	0.2 in/min; ASTM Test
	30.0 MPa @Temperature 120 °C	4350 psi @Temperature 248 °F	ASTM Test
	30.0 MPa @Temperature 120 °C	4350 psi @Temperature 248 °F	ISO Data
	40.0 MPa @Temperature 80.0 °C	5800 psi @Temperature 176 °F	ISO Data
	40.0 MPa @Temperature 80.0 °C	5800 psi @Temperature 176 °F	ASTM Test
	135 MPa @Temperature -40.0 °C	19600 psi @Temperature -40.0 °F	ASTM Test
	135 MPa @Temperature -40.0 °C	19600 psi @Temperature -40.0 °F	ISO Data
Tensile Strength, Ultimate	85.0 MPa	12300 psi	5mm/min; ISO 527
Elongation at Break	10 %	10 %	5mm/min; ISO 527
	10 %	10 %	0.2 in/min; ASTM Test
	6.0 % @Temperature -40.0 °C	6.0 % @Temperature -40.0 °F	ASTM Test
	6.0 % @Temperature -40.0 °C	6.0 % @Temperature -40.0 °F	ISO Data
	35 % @Temperature 80.0 °C	35 % @Temperature 176 °F	ISO Data
	35 % @Temperature 80.0 °C	35 % @Temperature 176 °F	ASTM Test
	40 % @Temperature 120 °C	40 % @Temperature 248 °F	ASTM Test
	40 % @Temperature 120 °C	40 % @Temperature 248 °F	ISO Data
Tensile Modulus	6.40 GPa	928 ksi	1mm/min; ISO 527
	0.970 GPa @Temperature 120 °C	141 ksi @Temperature 248 °F	ISO Data
	1.36 GPa @Temperature 80.0 °C	197 ksi @Temperature 176 °F	ISO Data
	8.31 GPa @Temperature -40.0 °C	1210 ksi @Temperature -40.0 °F	ISO Data
Flexural Strength	140 MPa	20300 psi	ISO Data
Flexural Modulus	5.20 GPa	754 ksi	ISO Data
Izod Impact, Notched (ISO)	6.00 kJ/m²	2.86 ft-lb/in²	ISO Test
Charpy Impact Unnotched	13.0 J/cm²	61.9 ft-lb/in²	ISO 179
Charpy Impact, Notched	0.300 J/cm²	1.43 ft-lb/in²	ISO 179
Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093
Thermal Properties	Metric	English	Comments
CTE, linear	50.0 µm/m-°C @Temperature -30.0 - 30.0 °C	27.8 µin/in-°F @Temperature -22.0 - 86.0 °F	ASTM Test
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test
Deflection Temperature at 0.46 MPa (66 psi)	190 °C	374 °F	ISO 75
Flammability, UL94	HB	HB
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in
Processing Properties	Metric	English	Comments
Melt Temperature	275 °C	527 °F	Injection molding
Mold Temperature	95.0 °C	203 °F	Injection molding
Descriptive Properties
Color	BK-102
Commercial Status	Active America
Form	Pellets
Impact Modified	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding
Special characteristic	Heat stabilized or stable to heat
	X
UL.UL-C	Yes