顆粒圖： 
、
、用途：
廣泛應(yīng)用于機(jī)械、儀器儀表、汽車部件、電子電氣、鐵路、家電、通訊、紡機(jī)、體育休閑用品、油管、油箱及一些精密工程制品。
電子電器：連接器、卷線軸、計(jì)時(shí)器、護(hù)蓋斷路器、開關(guān)殼座。
汽車： 散熱風(fēng)扇、門把、油箱蓋、進(jìn)氣隔柵、水箱護(hù)蓋、燈座。
工業(yè)零件：椅座、自行車輸框、溜冰鞋底座、紡織梭、踏板、滑輸。
上海松翰塑化科技有限公司，供應(yīng)原料，品質(zhì)真實(shí),物實(shí)價(jià)廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
歡迎各位客戶前來咨詢：
聯(lián)系人： 夏先生
手 機(jī)：13501802636
QQ ：205730283
郵 箱 ：205730283@qq.com
物性表:
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.4 % | 1.4 % | 24 hour; ISO Test | ||
| 8.2 % | 8.2 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.3 % | 2.3 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Measurement | 61 | 61 | Formic Acid | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ASTM Test | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.0 % | 2.0 % | 5mm/min; ISO 527 | ||
| 3.0 % | 3.0 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 5.70 GPa | 827 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 165 MPa | 23900 psi | ISO Data | ||
| Flexural Modulus | 4.80 GPa | 696 ksi | ISO Data | ||
| 5.38 GPa | 780 ksi | ASTM Test | |||
| Izod Impact, Notched | 0.450 J/cm @Thickness 3.17 mm |
0.843 ft-lb/in @Thickness 0.125 in |
ASTM Test | ||
| Izod Impact, Notched (ISO) | 4.50 kJ/m² | 2.14 ft-lb/in² | ISO Test | ||
| 4.00 kJ/m² @Temperature -40.0 °C |
1.90 ft-lb/in² @Temperature -40.0 °F |
ISO Test | |||
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179 | ||
| 0.300 J/cm² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 50.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
27.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM Test | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75 | ||
| 200 °C | 392 °F | ASTM Test | |||
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|||
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
||||
| De |
|||||
| Color | BK | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| UL.UL-C | Yes | ||||