| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183/A | ||
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | Isotropy | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | |||
| 0.0090 cm/cm | 0.0090 in/in | ISO 294-4 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 200 MPa | 29000 psi | ISO 527 Type 1A | ||
| Tensile Stress | 39.0 MPa @Strain 1.00 %, Temperature 200 °C |
5660 psi @Strain 1.00 %, Temperature 392 °F |
|||
| 45.0 MPa @Strain 2.00 %, Temperature 200 °C |
6530 psi @Strain 2.00 %, Temperature 392 °F |
||||
| 48.0 MPa @Strain 3.00 %, Temperature 200 °C |
6960 psi @Strain 3.00 %, Temperature 392 °F |
||||
| 50.0 MPa @Strain 4.00 %, Temperature 200 °C |
7250 psi @Strain 4.00 %, Temperature 392 °F |
||||
| 80.0 MPa @Strain 0.500 %, Temperature 23.0 °C |
11600 psi @Strain 0.500 %, Temperature 73.4 °F |
||||
| 150 MPa @Strain 1.00 %, Temperature 23.0 °C |
21800 psi @Strain 1.00 %, Temperature 73.4 °F |
||||
| 180 MPa @Strain 1.50 %, Temperature 23.0 °C |
26100 psi @Strain 1.50 %, Temperature 73.4 °F |
||||
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 Type 1A | ||
| Tensile Modulus | 15.0 GPa | 2180 ksi | ISO 527 Type 1A | ||
| Flexural Strength | 280 MPa | 40600 psi | ASTM D790 | ||
| 320 MPa | 46400 psi | ISO 178 | |||
| Flexural Modulus | 13.5 GPa | 1960 ksi | ISO 178 | ||
| 13.5 GPa | 1960 ksi | ASTM D790 | |||
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | ISO 180/1eA | ||
| Izod Impact, Unnotched (ISO) | 80.0 kJ/m² | 38.1 ft-lb/in² | ISO 180/1eU | ||
| Charpy Impact Unnotched | 8.50 J/cm² | 40.4 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.70 J/cm² | 8.09 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 263 °C | 505 °F | ISO 11357 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ISO 75/Bf | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | ISO 75/Af | ||
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
1210 | ||
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 | |||
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
1210 | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 265 - 275 °C | 509 - 527 °F | |||
| Mold Temperature | 80.0 - 110 °C | 176 - 230 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Moisture Content | <= 0.12 % | <= 0.12 % | |||
| De |
|||||
| Compression Zone | 270-280°C | ||||
| Mixing Zone | 280-290°C | ||||
應用：廣泛用于制造機械、汽車、化學與電氣裝置的零件，如齒輪、滾子、滑輪、輥軸、泵體中葉輪、風扇葉片、高壓密封圍、閥座、墊片、襯套、各種把手、支撐架、電線包內層等。