顆粒：
物性表:
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183/A | ||
| Water Absorption | 0.70 % @Temperature 23.0 °C, Time 86400 sec |
0.70 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 | ||
| Linear Mold Shrinkage | 0.0057 cm/cm | 0.0057 in/in | Isotropy | ||
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 230 MPa | 33400 psi | ISO 527 Type 1A | ||
| Tensile Strength, Yield | 230 MPa | 33400 psi | ISO 527 type 1 A | ||
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 Type 1A | ||
| Tensile Modulus | 13.8 GPa | 2000 ksi | ISO 527 Type 1A | ||
| Flexural Modulus | 11.0 GPa | 1600 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ISO 180/1eA | ||
| Charpy Impact Unnotched | 9.50 J/cm² | 45.2 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.55 J/cm² | 7.38 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Surface Resistance | 6.00e+13 ohm | 6.00e+13 ohm | IEC 60093 | ||
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243 | ||
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 | ||
| Comparative Tracking Index | 450 V | 450 V | Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 263 °C | 505 °F | ISO 11357 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75/Af | ||
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 | ||
| Oxygen Index | 23 % | 23 % | ISO 4589 | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |||
| Front Barrel Temperature | 280 - 300 °C | 536 - 572 °F | |||
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| De |
|||||
| Compression Zone | 270-300°C | ||||
廣泛用于制造機械、汽車、化學與電氣裝置的零件，如齒輪、滾子、滑輪、輥軸、泵體中葉輪、風扇葉片、高壓密封圍、閥座、墊片、襯套、各種把手、支撐架、電線包層等。亦可制成薄膜用作包裝材料。此外，還可用于制作醫療器械、體育用品、日用品等。
上海松翰塑化科技有限公司，供應原料，品質真實,物實價廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
歡迎各位客戶前來咨詢：