- 缺口沖擊強(qiáng)度: 0.325
- 拉伸強(qiáng)度 [MPa]: 75.0
- 斷裂伸長率 [%]: 135
- 彎曲模量 [MPa]: 7.05
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 6.25 GPa | 906 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 135 MPa | 19600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 7.05 GPa | 1020 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.325 J/cm | 0.609 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 8.00e+12 ohm | 8.00e+12 ohm | Internal Method |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 3.10 W/m-K | 21.5 BTU-in/hr-ft2-°F | Internal Method |
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C @Thickness 3.20 mm | 403 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Glass Transition Temp, Tg | 150 °C | 302 °F | ASTM D3482 |